Powder metallurgy of high-strength Al90.4Y4.4Ni4.3Co0.9 gas-atomized powder
verfasst von : K. G. Prashanth, K. B. Surreddi, S. Scudino, M. Samadi Khoshkhoo, Z. Wang, D. J. Sordelet, J. Eckert
Erschienen in: ICAA13 Pittsburgh
Verlag: Springer International Publishing
Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Al90.4Y4.4Ni4.3Co0.9 gas-atomized powder was hot pressed (HP) to produce highly dense bulk samples through combined devitrification and consolidation. The microstructure of the as-atomized powder is a mixture of amorphous phase with nanocrystalline fcc Al, whereas the consolidated samples consists of fcc Al and a series of intermetallic phases with or without residual amorphous phase depending on the hot pressing temperature (673 or 723 K). The HP samples exhibit a remarkable high strength of ~ 925 MPa (HP at 673 K) and ~ 820 MPa (HP at 723 K) combined with a plastic strain ranging between 14 and 30%. The reduction in strength for the sample HP at 723 K is linked to the complete crystallization of the powder with no residual amorphous phase.