Quasi-Static and Low-Velocity Impact Behavior of Injection Over-Molded Short/Continuous Fiber Reinforced Polypropylene Composites

verfasst von: Paramasivam Anandakumar, Mallina Venkata Timmaraju, Ramachandran Velmurugan

Erschienen in: Applied Composite Materials | Ausgabe 6/2023

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Over-molded composites (combination of continuous and short fiber reinforced composites) are materials of choice for production of relatively complex load-bearing structures due to their excellent structural performance, lightweight and lower assembly cost. The quasi-static and low-velocity impact behavior of over-molded polypropylene composites with continuous fiber face sheets and short fiber core were explored by conducting flexural, drop-weight impact and compression tests. Quasi-static test results revealed that over-molded specimens showed 43% and 33% higher flexural strength and flexural modulus, respectively, compared with short fiber composites. The over-molded composites showed significant improvement of impact peak load and absorbed energy compared with short fiber composites. Optical analysis of failed over-molded impact specimens revealed impact energy-absorption though interface debonding, delamination between plies of the top and bottom inserts and damage of the core. Finally, the laminated composite inserts at top and bottom of short glass fiber reinforced polypropylene lowered the impact damage and produced higher specific compression strength than the short glass fiber reinforced polypropylene.

Vorheriger Artikel Macroscopic Forming Simulation for a Unidirectional Non-crimp Fabric Using an Anisotropic Hyperelastic Material Model

Nächster Artikel Blast Response and Optimization Design of Polyurea-Coated Auxetic Honeycomb Sandwich Panels

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Polypropylene Compounds Market Size, Share & Trends Analysis Report By Product (Mineral Filled, Compounded TPO, Compounded TPV, Glass Fiber Reinforced, Talc Filled), By Application, By End-use, By Region, And Segment Forecasts, 2023 – 2030 Report ID: GVR-2-68038-734-6. (2018). https://www.grandviewresearch.com/industry-analysis/polypropylene-pp-compounds-market

Robert, M., Roy, R., Benmokrane, B.: Environmental Effects on Glass Fiber Reinforced Polypropylene Thermoplastic Composite Laminate for Structural Applications. Polym. Compos. 31(4), 604–611 (2009). https://doi.org/10.1002/pc.20834CrossRef

Passaro, A., Corvaglia, P., Manni, O., Barone, L., Maffezzoli, A.: Processing-properties relationship of sandwich panels with polypropylene-core and polypropylene-matrix composite skins. Polym. Compos. 25(3), 307–318 (2004). https://doi.org/10.1002/pc.20025CrossRef

Karger-Kocsis, J.: Instrumented impact fracture and related failure behavior in short-and long-glass-fiber-reinforced polypropylene. Compos. Sci. Tech. 48, 273–283 (1993). https://doi.org/10.1016/0266-3538(93)90144-6CrossRef

Rezaei, F., Yunus, R., Ibrahim, N.A., Mahdi, E.S.: Development of short-carbon-fiber-reinforced polypropylene composite for car bonnet. Polym. Plast. Tech. Eng. 47, 351–357 (2008). https://doi.org/10.1080/03602550801897323CrossRef

Fu, S.Y., Lauke, B., Mader, E., Yue, C.Y., Hu, X.: Tensile properties of short-glass-fiber-and short-carbon-fiber-reinforced polypropylene composites. Compos. Pt. A. Appl. Sci. Manuf. 31(10), 1117–1125 (2000)CrossRef

Puech, L., Ramakrishnan, K.R.L., Le Moigne, N., Corn, S., Slangen, P.R.: Investigating the impact behaviour of short hemp fibres reinforced polypropylene biocomposites through high speed imaging and finite element modeling. Compos. Pt. A- Appl. Sci. Manuf. 109, 428–439 (2018). https://doi.org/10.1016/j.compositesa.2018.03.013CrossRef

Mouti, Z., Westwood, K., Long, D., Njuguna, J.: An experimental investigation into localised low-velocity impact loading on glass fibre-reinforced polyamide automotive product. Compos. Struct. 104, 43–53 (2013). https://doi.org/10.1016/j.compstruct.2013.03.014CrossRef

Sarasua, J.R., Remiro, P.M., Pouyet, J.: The mechanical behaviour of PEEK short fibre composites. J. Mater. Sci. 30, 3501–3508 (1995). https://doi.org/10.1007/BF00349901CrossRef

10.

Garzon-Hernandez, S., Garcia-Gonzalez, D., Arias, A.: Multi-impact mechanical behaviour of short fibre reinforced composites. Compos. Struct. 202, 241–252 (2018). https://doi.org/10.1016/j.compstruct.2018.01.070CrossRef

11.

Bondy, M., Altenhof, W.: Low velocity impact testing of direct/inline compounded carbon fibre/ polyamide-6 long fibre thermoplastics. Int. J. Impact. Eng. 111, 66–76 (2018). https://doi.org/10.1016/j.ijimpeng.2017.08.012CrossRef

12.

Sorentino, L., Simeoli, S., Lannace, S.: Mechanical Performance Optimization through Interface Strength Gradation in PP/ Glass Fibre Reinforced Composites. Compos. Pt. B- Eng. 76, 201–208 (2015). https://doi.org/10.1016/j.compositesb.2015.02.026CrossRef

13.

Yudhanto, A., Wafai, H., Lubineau, G., Gautham, S., Mulle, M., Yaldiz, R., Verghese, N.: Revealing the effects of matrix behavior on low-velocity impact response of continuous fiber-reinforced thermoplastic laminates. Compos. Struct. 210, 239–249 (2019). https://doi.org/10.1016/j.compstruct.2018.11.040CrossRef

14.

Dogan, A.: Single and repeated low-velocity impact response of E-glass fiber-reinforced epoxy and polypropylene composites for different impactor shapes. J. Thermoplas. Compos. 35, 1–17 (2019). https://doi.org/10.1177/2F0892705719886911CrossRef

15.

Russo, P., Acierno, D., Simeoli, G., et al.: Flexural and impact response of woven glass fiber fabric/polypropylene composites. Compos. Pt. B- Eng. 54, 415–421 (2013). https://doi.org/10.1016/j.compositesb.2013.06.016CrossRef

16.

Jayashree, N.A., Airale, A.G., Ferraris, A., Messana, A., Sisca, L., Carello, M.: Process analysis for structural optimisation of thermoplastic composite component using the building block approach. Compos. Pt. B- Eng. 126, 119–132 (2017). https://doi.org/10.1016/j.compositesb.2017.06.007CrossRef

17.

Sealy, C.: Molding the future: ENGEL takes composite approach to composites. Reinf Plast. 60, 138–141 (2016). https://doi.org/10.1016/j.repl.2015.12.077CrossRef

18.

Andrzejewski, J., Przyszczypkowski, P., Szostak, M.: Development and characterization of poly(ethylene terephthalate) based injection molded self-reinforced composites. Direct reinforcement by overmolding the composite inserts. Mater. Des. 153, 273–286 (2018). https://doi.org/10.1016/j.matdes.2018.04.084CrossRef

19.

Fu, L., Zhang, M., Zhai, Z., Jiang, F.: The influence of preheating temperature on the mechanical properties of injection-overmolded hybrid glass fiber reinforced thermoplastic composites. Polym. Test. 105, 1–8 (2022). https://doi.org/10.1016/j.polymertesting.2021.107425CrossRef

20.

Wakeman, M.D., Hagstrand, P.O., Bonjour, F., Bourban, P.E., Manson, J.A.E.: Robotic tow placement for local reinforcement of glass mat thermoplastics (GMTs). Compos. Pt. A- Appl. Sci. Manuf. 33, 1199–1208 (2002). https://doi.org/10.1016/S1359-835X(02)00086-6CrossRef

21.

Febra, T., Ferreira, J.A.M., Costa, D., Da Silva, J., Capela, C.: Response of fabric insert injection overmolding pp based composites subjected to single and muti-impact. Fract. Struct. Inte. 48, 242–248 (2019). https://doi.org/10.3221/IGF-ESIS.48.25CrossRef

22.

Wis, A.A., Kodal, M., Ozturk, S.: Overmolded polylactide/jute-mat eco-composites: A new method to enhance the properties of natural fiber biodegradable composites. J. Appl. Polym. Sci. 137, 48692 (2019). https://doi.org/10.1002/app.48692CrossRef

23.

Alwekar, S., Ogle, R., Kim, S., Vaidya, U.: Manufacturing and characterization of continuous fiber-reinforced thermoplastic tape over-molded long fiber thermoplastic. Compos. Pt. B. Eng. 207, 108597 (2021). https://doi.org/10.1016/j.compositesb.2020.108597CrossRef

24.

Anandakumar, P., Timmaraju, M.V., Velmurugan, R.: Development of efficient short/continuous fiber thermoplastic composite automobile suspension upper control arm. Mater Today Proc. 39, 1187–1191 (2020). https://doi.org/10.1016/j.matpr.2020.03.543CrossRef

25.

Anandakumar, P., Timmaraju, M.V., Velmurugan, R.: Influence of preheating on the fracture behavior of over-molded short/continuous fiber reinforced polypropylene composites. J. Compos. Mater. 55, 1–10 (2021). https://doi.org/10.1177/2F00219983211038615CrossRef

26.

Zhang, Y., Sun, L., Li, L., Wang, T., Shen, L.: Experimental and numerical investigations on low-velocity impact response of high strength steel/composite hybrid plate. Int. J. Impact. Eng. 123, 1–13 (2019). https://doi.org/10.1016/j.ijimpeng.2018.08.015CrossRef

27.

Ghelli, D., Minak, G.: Low velocity impact and compression after impact tests on thin carbon/epoxy laminates. Compos. Pt. B- Eng. 42, 2067–2079 (2011). https://doi.org/10.1016/j.compositesb.2011.04.017CrossRef

28.

Ahmed, A., Bingjie, Z., Ikbal, M.H., Qingtao, W., Obed, A., Wei, L.: Experimental study on the effects of stacking sequence on low velocity impact and quasi-static response of foam sandwich composite structures. Adv. Struct. Eng. 18, 11 (2015). https://doi.org/10.1260/2F1369-4332.18.11.1789CrossRef

29.

Evci, C., Gulgec, M.: An experimental investigation on the impact response of composite materials. Int. J. Impact. Eng. 43, 40–51 (2012). https://doi.org/10.1016/j.ijimpeng.2011.11.009CrossRef

30.

Shim, V.P.W., Yang, L.M.: Characterization of the residual mechanical properties of woven fabric reinforced composites after low-velocity impact. Int. J. Mech. Scs. 47, 647–665 (2005). https://doi.org/10.1016/j.ijmecsci.2005.01.014CrossRef

31.

Hosur, M.V., Mohammed, A.A., Zainuddin, S., Jeelani, S.: Processing of nanoclay filled sandwich composites and their response to low-velocity impact loading. Compos. Struct. 82, 101–116 (2008). https://doi.org/10.1016/j.compstruct.2006.12.009CrossRef

32.

Jang, J., Moon, S.I.: Impact behavior of carbon fiber/ ultra-high modulus polyethylene fiber hybrid composites. Polym. Compos. 16, 325–329 (1995). https://doi.org/10.1002/pc.750160410CrossRef

33.

Sarasini, F., Tirillo, J., Ferrante, L., Valente, M., Valente, T., Lampani, L.: Drop-weight impact behaviour of woven hybrid basalt–carbon/epoxy composites. Compos. Pt. B- Eng. 59, 204–220 (2014). https://doi.org/10.1016/j.compositesb.2013.12.006CrossRef

34.

Shanmugam, L., Kazemi, M.E., Li, Z., Luo, W., Xiang, Y., Yang, L., Yang, J.: Low-velocity impact behavior of UHMWPE fabric/thermoplastic laminates with combined surface treatments of polydopamine and functionalized carbon nanotubes. Compos. Comms. 22, 100–527 (2020). https://doi.org/10.1016/j.coco.2020.100527CrossRef

Titel: Quasi-Static and Low-Velocity Impact Behavior of Injection Over-Molded Short/Continuous Fiber Reinforced Polypropylene Composites
verfasst von: Paramasivam Anandakumar
Mallina Venkata Timmaraju
Ramachandran Velmurugan
Publikationsdatum: 14.09.2023
Verlag: Springer Netherlands
Erschienen in: Applied Composite Materials / Ausgabe 6/2023
Print ISSN: 0929-189X
Elektronische ISSN: 1573-4897
DOI: https://doi.org/10.1007/s10443-023-10163-3

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 6/2023

Investigating Damage Mechanisms in Cord-Rubber Composite Air Spring Bellows of Rail Vehicles and Representative Specimen Design

Design and Strengthening Mechanisms of Dual-Phase Lattice Energy-Absorbing Structure Based On Shear-Banding Controlling

Dynamic Fracture Toughness and Damage Monitoring in Hybrid Composites

Identification of Spatial Modulus Distribution of Chopped Carbon Fiber Tape-reinforced Thermoplastic Structures Using Modal Test-based Inverse Analysis

Mechanical Properties and Thermal Oxygen Corrosion Behavior of Al2O3f-CF Hybrid Fiber Reinforced Ceramicizable Phenolic Resin Matrix Composites

Advances in Preparation Methods and Conductivity Properties of Graphene-based Polymer Composites

Premium Partner

Marktübersichten