Size-controlled synthesis of BiFeO3 nanoparticles by a soft-chemistry route

verfasst von: H. Yang, T. Xian, Z. Q. Wei, J. F. Dai, J. L. Jiang, W. J. Feng

Erschienen in: Journal of Sol-Gel Science and Technology | Ausgabe 1/2011

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In this work we report the size-controlled synthesis of BiFeO3 nanoparticles via a soft-chemistry route. In this route, the aqueous solution of inorganic Bi and Fe salt is gelled by using acrylamide and bisacrylamide. It is demonstrated that the grain size of resulted BiFeO3 powders can be tailored by varying the ratio of acrylamide to bisacrylamide. With increase in the bisacrylamide content, the grain size decreases monotonously. By using this method, a series of BiFeO3 samples with average grain size ranging from 110 to 52 nm have been prepared. The thermal decomposition process of precursor xerogels and the formation of BiFeO3 phase are investigated by means of X-ray diffraction, thermogravimetric analysis, differential scanning calorimetry analysis, and fourier transform infrared spectroscopy (FTIR). SEM observations reveal that the prepared BiFeO3 nanoparticles are nearly spherical in shape with a narrow diameter distribution. Magnetic hysteresis loop measurement shows that the BiFeO3 nanoparticles exhibit weak ferromagnetic behavior at room temperature, and a saturation magnetization of ~1.56 emu/g is achieved for the 52 nm sample.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Literatur
2.
Zurück zum Zitat Fiebig M, Lottermoser Th, Fröhlich D, Goltsev AV, Pisarev RV (2002) Nature (London) 419:818 Fiebig M, Lottermoser Th, Fröhlich D, Goltsev AV, Pisarev RV (2002) Nature (London) 419:818
3.
Zurück zum Zitat Michel C, Moreau J-M, Achenbach GD, Gerson R, James WJ (1969) Solid State Commun 7:701CrossRef Michel C, Moreau J-M, Achenbach GD, Gerson R, James WJ (1969) Solid State Commun 7:701CrossRef
4.
Zurück zum Zitat Moreau J-M, Michel C, Gerson R, James WJ (1971) J Phys Chem Solids 32:1315CrossRef Moreau J-M, Michel C, Gerson R, James WJ (1971) J Phys Chem Solids 32:1315CrossRef
5.
Zurück zum Zitat Tabares-Munoz C, Rivera JP, Monnier A, Schmid H (1985) Jpn J Appl Phys. Suppl 24:1051 Tabares-Munoz C, Rivera JP, Monnier A, Schmid H (1985) Jpn J Appl Phys. Suppl 24:1051
6.
Zurück zum Zitat Fischer P, Polomska M, Sosnowska I, Szymanksi M (1980) J Phys C 13:1931CrossRef Fischer P, Polomska M, Sosnowska I, Szymanksi M (1980) J Phys C 13:1931CrossRef
7.
Zurück zum Zitat Sosnowska I, Peterlin-Neumaier T, Steichele E (1982) J Phys C 15:4835CrossRef Sosnowska I, Peterlin-Neumaier T, Steichele E (1982) J Phys C 15:4835CrossRef
8.
Zurück zum Zitat Ederer C, Spaldin NA (2005) Phys Rev B 71:060401(R) Ederer C, Spaldin NA (2005) Phys Rev B 71:060401(R)
9.
Zurück zum Zitat Luo WJ, Wang DL, Peng XD, Wang FW (2009) J. Sol Gel Sci Technol 51:53CrossRef Luo WJ, Wang DL, Peng XD, Wang FW (2009) J. Sol Gel Sci Technol 51:53CrossRef
10.
11.
Zurück zum Zitat Xie SH, Li JY, Proksch R, Liu YM, Zhou YC, Liu YY, Ou Y, Lan LN, Qiao Y (2008) Appl Phys Lett 93:222904CrossRef Xie SH, Li JY, Proksch R, Liu YM, Zhou YC, Liu YY, Ou Y, Lan LN, Qiao Y (2008) Appl Phys Lett 93:222904CrossRef
13.
Zurück zum Zitat Mazumder R, Devi PS, Bhattacharya D, Choudhury P, Sen A, Raja M (2007) Appl Phys Lett 91:062510CrossRef Mazumder R, Devi PS, Bhattacharya D, Choudhury P, Sen A, Raja M (2007) Appl Phys Lett 91:062510CrossRef
14.
Zurück zum Zitat Park TJ, Papaefthymiou GC, Viescas AJ, Moodenbaugh AR, Wong SS (2007) Nano Lett 7:766CrossRef Park TJ, Papaefthymiou GC, Viescas AJ, Moodenbaugh AR, Wong SS (2007) Nano Lett 7:766CrossRef
16.
Zurück zum Zitat Chen C, Cheng JR, Yu SW, Che LJ, Meng ZY (2006) J Cryst Growth 291:135CrossRef Chen C, Cheng JR, Yu SW, Che LJ, Meng ZY (2006) J Cryst Growth 291:135CrossRef
17.
18.
19.
Zurück zum Zitat Cho CM, Noh JH, Cho I-S, An J-S, Hong KS, Kim JY (2008) J Am Ceram Soc 91:3753CrossRef Cho CM, Noh JH, Cho I-S, An J-S, Hong KS, Kim JY (2008) J Am Ceram Soc 91:3753CrossRef
20.
Zurück zum Zitat Wang YG, Xu G, Yang LL, Ren ZH, Wei X, Weng WJ, Du PY, Shen G, Han GR (2009) Ceram Int 35:1285CrossRef Wang YG, Xu G, Yang LL, Ren ZH, Wei X, Weng WJ, Du PY, Shen G, Han GR (2009) Ceram Int 35:1285CrossRef
21.
Zurück zum Zitat Chaudhuri A, Mitra S, Mandal M, Mandal K (2010) J Alloys Compd 491:703CrossRef Chaudhuri A, Mitra S, Mandal M, Mandal K (2010) J Alloys Compd 491:703CrossRef
22.
23.
Zurück zum Zitat Prado-Gonjal J, Villafuerte-Castrejo ME, Fuentes L, Mora E (2009) Mater Res Bull 44:1734CrossRef Prado-Gonjal J, Villafuerte-Castrejo ME, Fuentes L, Mora E (2009) Mater Res Bull 44:1734CrossRef
24.
25.
26.
28.
29.
Zurück zum Zitat Selbach SM, Tybell T, Einarsrud M-A, Grande T (2007) Chem Mater 19:6478CrossRef Selbach SM, Tybell T, Einarsrud M-A, Grande T (2007) Chem Mater 19:6478CrossRef
30.
31.
32.
Zurück zum Zitat Xian T, Yang H, Shen X, Jiang JL, Wei ZQ, Feng WJ (2009) J Alloys Compd 480:889CrossRef Xian T, Yang H, Shen X, Jiang JL, Wei ZQ, Feng WJ (2009) J Alloys Compd 480:889CrossRef
33.
34.
35.
Zurück zum Zitat Yang H, Cao ZE, Shen X, Jiang JL, Wei ZQ, Dai JF, Feng WJ (2009) Mater Lett 63:655CrossRef Yang H, Cao ZE, Shen X, Jiang JL, Wei ZQ, Dai JF, Feng WJ (2009) Mater Lett 63:655CrossRef
36.
Zurück zum Zitat Yang H, Cao ZE, Shen X, Xian T, Feng WJ, Jiang JL, Feng YC, Wei ZQ, Dai JF (2009) J Appl Phys 106:104317CrossRef Yang H, Cao ZE, Shen X, Xian T, Feng WJ, Jiang JL, Feng YC, Wei ZQ, Dai JF (2009) J Appl Phys 106:104317CrossRef
37.
39.
40.
Zurück zum Zitat Kumar MM, Palkar VR, Srinivas K, Suryanarayana SV (2000) Appl Phys Lett 76:2764CrossRef Kumar MM, Palkar VR, Srinivas K, Suryanarayana SV (2000) Appl Phys Lett 76:2764CrossRef
41.
Zurück zum Zitat Klug MP, Alexander LE (1974) X-ray diffraction procedure for polycrystalline and amorphous materials. Wiley, New York, p 634 Klug MP, Alexander LE (1974) X-ray diffraction procedure for polycrystalline and amorphous materials. Wiley, New York, p 634
42.
Metadaten
Titel
Size-controlled synthesis of BiFeO3 nanoparticles by a soft-chemistry route
verfasst von
H. Yang
T. Xian
Z. Q. Wei
J. F. Dai
J. L. Jiang
W. J. Feng
Publikationsdatum
01.04.2011
Verlag
Springer US
Erschienen in
Journal of Sol-Gel Science and Technology / Ausgabe 1/2011
Print ISSN: 0928-0707
Elektronische ISSN: 1573-4846
DOI
https://doi.org/10.1007/s10971-010-2383-6

Weitere Artikel der Ausgabe 1/2011

Journal of Sol-Gel Science and Technology 1/2011 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.