13. Stress Corrosion Cracking and Corrosion-Fatigue

verfasst von : Pietro Pedeferri (Deceased)

Erschienen in: Corrosion Science and Engineering

Verlag: Springer International Publishing

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

When a susceptible metal is in contact with a specific environment, in presence of a tensile stress exceeding a threshold, the corrosion-enhanced formation of cracks and catastrophic failure is called stress corrosion cracking (SCC). Although infrequent, consequences are so dangerous that it deserves to be described in details: in this chapter, after the introduction of the SCC mechanism, mechanical, metallurgical and environmental factors at its basis are explained, and specific preventative measurements are suggested. Another form of degradation that links mechanical stress and corrosion, i.e., corrosion-fatigue, is also described.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Crevice Corrosion

Nächstes Kapitel Hydrogen-Induced Damage

Brown BF (1968) The application of fracture mechanics to stress corrosion cracking. Met Rev 156:55

Brown BF (1971) The theory of SCC in alloys. Im: Scully JC (ed) NATO Scientific Affairs Division, Brussels

Brown BF (1977) SCC control measures. NBS Monograph 156, National Bureau of Standard, Washington DC

Copson HR (1959) Physical metallurgy of stress corrosion fracture. Interscience, New York, p. 247

Denhard EE (1960) Effect of composition and heat treatment on the stress corrosion cracking of austenitic stainless steels. Corrosion 16(7):359t–370t

Fontana M (1986) Corrosion engineering, 3rd edn. McGraw-Hill, New York. ISBN 0-07-100360-6

Henthorne M (2016) The slow strain rate stress corrosion cracking test—a 50 year retrospective. Corrosion 12(72):1458–1518

Magnin T, Chambreuil A, Bayle B (1996) The corrosion-enhanced plasticity model for stress corrosion cracking in ductile FCC alloys. Acta Mater 44(4):1457–1470CrossRef

Parkins RN, Fessler RR, Boyd WK (1972) Stress corrosion cracking of carbon steel in carbonate solutions. Corrosion 28(8):313–320CrossRef

Parkins RN, Wearmouth WR, Dean GP (1973) Role of stress in the stress corrosion cracking of a Mg-Al Alloy. Corrosion 29(6):251–260CrossRef

Sedriks AJ (1996) Corrosion of stainless steels, 2nd edn. Wiley, New York

Sinigaglia D, Re G, Pedeferri P (1979) Cedimento per fatica e ambientale dei materiali metallici. CLUP, Milano, Italy (in italian)

Staehle RW (1977) Predictions and experimental verification of the slip dissolution model for stress corrosion cracking of low strength alloys. In: Staehle RW, Hochmann J, McCright RD, Slater JE (eds) NACE-5 Stress corrosion cracking and hydrogen embrittlement of iron base alloys. NACE International, Houston

Titel: Stress Corrosion Cracking and Corrosion-Fatigue
verfasst von: Pietro Pedeferri (Deceased)
Verlag: Springer International Publishing
Buch: Corrosion Science and Engineering
Print ISBN: 978-3-319-97624-2

Electronic ISBN: 978-3-319-97625-9

Copyright-Jahr: 2018
DOI: https://doi.org/10.1007/978-3-319-97625-9_13

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht