Structural investigations of V₂O₅–P₂O₅–CaO glass system by FT-IR and EPR spectroscopies

xV₂O₅·(100 − x)[0.7P₂O₅·0.3CaO] glass system was obtained for 0 ≤ x ≤ 35 mol% V₂O₅. In order to obtain information regarding their structure, several techniques such as X-Ray diffraction, FT-IR, and EPR spectroscopies were used. X-Ray diffraction patterns of investigated samples are characteristic of vitreous solids. FT-IR spectra of 0.7P₂O₅·0.3CaO glass matrix and its deconvolution show the presence in the glass structure of all structural units characteristic to P₂O₅. Their number are increasing for x ≤ 3 mol% V₂O₅ then, for higher content of vanadium ions, the number of phosphate structural units are decreasing leading to a depolymerization of the structure. The structural units characteristic to V₂O₅ were not evidenced but their contribution to the glass structure can be clearly observed. EPR revealed a well resolved hyperfine structure (hfs) typical for vanadyl ions in a C_4v symmetry for x ≤ 3 mol% V₂O₅. For 5 < x < 20 mol% V₂O₅ the spectra show a superposition of two EPR signals one due to a hfs structure and another consisting of a broad line typical for associated V⁴⁺–V⁴⁺ ions. For x ≥ 20 mol% V₂O₅ only the broad line can be observed. The composition dependence of the line-width suggests the presence of dipole–dipole interaction between vanadium ions up to x ≤ 5 mol% V₂O₅ and superexchange interactions between vanadium ions for x > 5 mol% V₂O₅.