Study on Hold-Time Effects in Environmental Fatigue Lifetime of Low-Alloy Steel and Austenitic Stainless Steel in Air and Under Simulated PWR Primary Water Conditions

verfasst von : M. Herbst, A. Roth, J. Rudolph

Erschienen in: Proceedings of the 18th International Conference on Environmental Degradation of Materials in Nuclear Power Systems – Water Reactors

Verlag: Springer International Publishing

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

This paper summarizes the results of a research project on environmental effects on the fatigue lifetime of selected low-alloy steels and austenitic stainless steels. Results from investigations on the effect of hold times during fatigue in air, as well as under simulated PWR primary water conditions are presented. Strain controlled fatigue tests with low strain rates and low strain amplitudes have been performed in air using a low-alloy RPV steel as well as the stabilized austenitic stainless steel 347 and the non-stabilized austenitic stainless steel 304L. Similar strain controlled tests under simulated PWR primary coolant conditions were performed using the two above mentioned austenitic stainless steels. The fatigue cycling was performed at 240 °C whereas holds were applied at higher temperature (290 °C). The effect of hold periods is compared to reference tests without hold times and to the prediction based on NUREG/CR 6909, Rev. 1.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Mechanistic Understanding of Environmentally Assisted Fatigue Crack Growth of Austenitic Stainless Steels in PWR Environments

Nächstes Kapitel Evaluation of Additively Manufactured Materials for Nuclear Plant Components

O.K. Chopra, W.J. Shack, Effect of LWR coolant on the fatigue life of reactor materials. U.S. NRC, NUREG/CR-6909, ANL-06/08 (2006)

A. Roth, B. Devrient, Environmental effects on fatigue—possible reasons for the apparent mismatch between laboratory test results and operational experience. FONTEVRAUD 7—Contribution of Materials Investigations to Improve the Safety and Performance of LWRs (2010)

J. Solin, J. Alhainen, E. Karabaki et al., Effects of hot water and holds on fatigue of stainless steel, in ASME 2016 Pressure Vessels and Piping Conference, V01AT01A021 (2016)

J. Solin, S. Reese, H.E. Karabaki et al., Environmental fatigue factors (NUREG/CR-6909) and strain controlled data for stabilized austenitic stainless steel, in ASME 2013 Pressure Vessels and Piping Conference, V01AT01A021 (2013)

J. Solin, S. Reese, H.E. Karabaki et al., Fatigue of stainless steel in simulated operational conditions: effects of PWR water, temperature and holds, in ASME 2014 Pressure Vessels and Piping Conference, V001T01A027 (2014)

J. Solin, S. Reese, H.E. Karabaki et al., Research on hold time effects in fatigue of stainless steel: simulation of normal operation between fatigue transients, in ASME 2015 Pressure Vessels and Piping Conference, V01AT01A030

J. Solin, E. Karabaki, W. Mayinger, Effects of hot water and holds on fatigue of stainless steel, in Proceedings of the ASME 2016 Pressure Vessels and Piping Conference, PVP 2016, July 17–21, Vancouver, British columbia, Canada, PVP2016-63291 (2016)

J.A. Le Duff, A. Lefrancois, J. Vernot, Effects of surface finish and loading conditions on the low cycle fatigue behaviour of austenitic stainless steel in PWR environment for various strain amplitude levels, Proceedings of ASME 2009 PVP(PVP2009-78129)

J.A. Le Duff, A. Lefrançois, J.P. Vernot, Effects of surface finish and loading conditions on the low cycle fatigue behavior of austenitic stainless steel in PWR environment: comparison of LCF test results with NUREG/CR-6909 life estimations, in ASME 2008 Pressure Vessels and Piping Conference, pp. 451–460

10.

J.A. Le Duff, A. Lefrançois, J.P. Vernot et al., Effect of loading signal shape and of surface finish on the low cycle fatigue behavior of 304L stainless steel in PWR environment, in ASME 2010 Pressure Vessels and Piping Division/K-PVP Conference, pp. 233–241

11.

J.A. Le Duff, A. Lefrançois, J.P. Vernot, D. Bossu, Effect of loading signal shape and of surface finish on the low cycle fatigue behavior of 304L stainless steel in PWR environment. PVP2010-26027, in Proceedings of the ASME 2010 Pressure Vessels & Piping Conference PVP2010, Bellevue, Washington, USA, 18–22 July 2010

12.

M. Kammerer, K.-H. Herter, X. Schuler, Untersuchungen zu Belastungsparametern und Mediumseinfluss auf die Ermüdungsfestigkeit austenitischer und ferritischer Stähle einschließlich Schweißverbindungen, Abschlussbericht BMWi Vorhaben 1501459A (2017)

13.

A. Roth, M. Herbst, J. Rudolph et al., Environmental influences on the fatigue assessment of austenitic and ferritic steel components including welds, in Proceedings of the ASME 2014 Pressure Vessels & Piping Conference PVP2014 (2014)

14.

J. Rudolph, P. Wilhelm, M. Kammerer, K.-H. Herter, X. Schuler, Verbundvorhaben: „Untersuchungen zum Einfluss bauteilrelevanter Beanspruchungen auf die Ermüdungsfestigkeit austenitischer und ferritischer Stähle einschließlich Schweißverbingungen“ AP8 „Entwicklung von Ansätzen für ein ingeniertechnisch handhabbares Berechnungskonzept“ (2017)

15.

H.-P. Seifert, S. Ritter, Environmentally-assisted cracking in austenitic light water reactor structural materials—final report of the KORA-I project. Report: Paul Scherrer Institute, 2009, Paul Scherrer Institute: Nuclear Energy and Safety Research Department, Villigen (Switzerland). PSI Report No. 09––03 (2009)

16.

H.-P. Seifert, S. Ritter, H.J. Leber, Corrosion fatigue crack growth behaviour of austenitic stainless steels under light water reactor conditions. Corros. Sci. 55, 61–75 (2012)CrossRef

17.

H.-P. Seifert, S. Ritter, H. Leber, Effect of static load hold periods on the corrosion fatigue behaviour of austenitic stainless steels in simulated BWR environments, in Conference: 15th International Conference on Environmental Degradation of Materials in Nuclear Systems—Water Reactors, Colorado Springs (Colorado, USA). No. 0547, pp. 547–560, 7–11 Aug 2011CrossRef

18.

E. Karabaki, M. Twite, J. Solin et al., Fatigue performance of stainless steels (304L, 347) in experiments simulating NPP operation with hold times, in ASME 2016 Pressure Vessels and Piping Conference, V01AT01A014 (2016)

19.

E. Karabaki, J. Solin, M. Twite, M. Herbst, J. Mann, M. Grace Burke, Fatigue with hold times simulating NPP normal operation results for stainless steel grades 304L and 347, in Proceedings of the ASME 2017 Pressure Vessels & Piping Division Conference, PVP2017, PVP2017-66097

20.

K. Kußmaul et al. Rißwachstum von rohrförmigen Komponenten mit Umfangsfehlern bei Innendruckbelastung und überlagertem wechselnden äußeren Biegemoment. Staatliche Materialprüfungsanstalt Universität Stuttgart. Abschlussbericht, MPA-Auftrags-Nr. 8530 00 000, Band 1, 04/1993

21.

M. Herbst, A. Roth, Untersuchungen zum Einfluss bauteilrelevanter Beanspruchungen auf die Ermüdungsfestigkeit austenitischer und ferritischer Stähle einschließlich Schweißverbindungen, Teilprojekt B: Untersuchungen zum Einfluss von Haltezeiten und Mediumseinfluss auf die Ermüdungsfestigkeit austenitischer und ferritischer Stähle, Abschlussbericht BMWi Vorhaben 1501459B (2017)

22.

J. Rudolph, P. Wilhelm, A. Roth, M. Herbst, M. Kammerer, K.-H. Herter, X. Schuler, Proposal for an improved engineering fatgue lifetime assessment concept, in Proceedings of the ASME 2016 Pressure Vessels and Piping Conference, PVP 2016, Vancouver, British columbia, Canada, PVP2016-63576, July 17–21, 2016

Titel: Study on Hold-Time Effects in Environmental Fatigue Lifetime of Low-Alloy Steel and Austenitic Stainless Steel in Air and Under Simulated PWR Primary Water Conditions
verfasst von: M. Herbst
A. Roth
J. Rudolph
Verlag: Springer International Publishing
Buch: Proceedings of the 18th International Conference on Environmental Degradation of Materials in Nuclear Power Systems – Water Reactors
Print ISBN: 978-3-030-04638-5

Electronic ISBN: 978-3-030-04639-2

Copyright-Jahr: 2019
DOI: https://doi.org/10.1007/978-3-030-04639-2_62

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht