Synthesis of poly[2-(perfluorooctyl)ethyl acrylate-co-poly(ethylene glycol) methacrylate] and its control of enzyme activity in supercritical carbon dioxide

Poly[2-(perfluorooctyl)ethyl acrylate-co-poly(ethylene glycol) methacrylate], P(POA-co-PEGm) was prepared as a new surfactant for scCO₂. The random copolymer was obtained by the radical polymerization of 2-(perfluorooctyl)ethyl acrylate (POA) and poly(ethylene glycol) methacrylate (PEGm) in DMF. The molar ratio of the POA and PEGm units in the copolymer was POA/PEGm = 0.972/0.028 by ¹H NMR. The molecular weight and molecular weight distribution were estimated by size exclusion chromatography to be Mn = 133,000 and Mw/Mn = 8.25, respectively. It was suggested that the copolymer formed micellar aggregates with the cores of the PEGm chains in scCO₂, based on the analyses of the copolymer in hexafluorobenzene by ¹H NMR and dynamic light scattering. The copolymer was soluble in scCO₂ and had a cloud point at a much higher pressure than the critical pressure. It was found that the copolymer solubilized CO₂-insoluble proteins such as bovine serum albumin and subtilisin Carlsberg in scCO₂. The solubility of the copolymer was not influenced by the presence of the proteins; however, the solubility decreased in the presence of a small amount of water along with the protein. The activity of the subtilisin slightly decreased when only placed in scCO₂, whereas a marked decrease in the activity was observed for the subtilisin in the presence of the copolymer in scCO₂. The subtilisin activity decreased as the CO₂ pressure increased.