Synthesis of rod-like mesoporous silica with hexagonal appearance using sodium silicate as precursor
Erschienen in: Colloid and Polymer Science | Ausgabe 7/2004
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Using sodium silicate as precursor, rod-like mesoporous silica with hexagonal appearance was synthesized by controlling the pH value of a mixed micelles solution of cetyltrimethylammonium bromide (CTAB) and cetyltrimethylammonium chloride (CTAC) during hydrolysis of ethyl acetate. The resulting mesoporous silica was characterized by small angle X-ray diffraction, nitrogen gas adsorption-desorption measurement and scanning electron microscopy. Results showed that the regular rod-like shapes with hexagonal appearance were obtained at a 9:1 molar ratio of CTAB to CTAC, and that the amounts and lengths of the rod-like mesoporous silica particles decreased with decreasing CTAB to CTAC molar ratio. There existed a type IV adsorption isotherm and an H1 hysteresis loop in N2 gas adsorption-desorption curves.