01.06.2012 | Technical Article---Peer-Reviewed
Turbine Shroud Cracking Investigation and Repair
Erschienen in: Journal of Failure Analysis and Prevention | Ausgabe 3/2012
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Outer shroud segments fabricated from a cast 310 stainless steel were found to have cracked following extended service. Several of these cracked shrouds were sent to the GE-Poland Materials Laboratory for metallurgical investigation with a view to determine the cause of cracking. Detailed investigation revealed cracking to be associated with a sigma phase, a brittle TCP intermetallic, which had developed over time during engine operation. Initial attempts to weld repair the cracks proved unsuccessful as cracks were discovered both during and after the weld repair procedure. A new weld repair procedure incorporating a pre-weld solution annealing heat treatment to remove the sigma phase before welding was successfully developed, thus alleviating the cracking concern.