A Developed Method for Fabricating In-Situ TiC _p /Mg Composites by Using Quick Preheating Treatment and Ultrasonic Vibration

Quick preheating treatment of the Al-Ti-C pellets and high-intensity ultrasonic vibration are introduced in the fabrication of in-situ TiC _p /Mg composites. Al-Ti-C pellets are preheated for about 130 seconds in the furnace at 1023 K (750 °C), in which magnesium is melted as well. In this process, plenty of heat can be accumulated due to the reactive diffusion between liquid aluminum and solid titanium in Al-Ti-C, and a small amount of Al₃Ti phase is formed as well. After adding the preheated Al-Ti-C into the molten magnesium, thermal explosion takes place in a few seconds. In the meantime, high-intensity ultrasonic vibration is applied into the melt to disperse in-situ formed TiC particles into the matrix and degas the melt as well. Microstructural characterization indicates that in-situ formed TiC particles are spherical in morphology and smaller than 2 μm in size. Furthermore, a homogeneous microstructure with low porosity of the magnesium composite is obtained due to the effect of ultrasonic vibration. A novel approach using the quick preheating treatment technique and high-intensity ultrasonic vibration to synthesize in-situ TiC _p /Mg composites is proposed in our research.