Age Hardening of the Al0.5CoCrNiTi0.5 High-Entropy Alloy
Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 1/2014
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Al0.5CoCrNiTi0.5 high-entropy alloy was synthesized by vacuum arc melting in a copper mold. This alloy was aged at 773 K to 1473 K (500 °C to 1200 °C) for 24 hours to investigate the microstructure and hardness. The hardness of the as-cast alloy is HV743, and it exhibits a dendritic structure, in which dendrite is composed of body-centered cubic (bcc), face-centered cubic (fcc), and σ phases, and interdendrite is an eutectic structure consisting of bcc and order bcc phases. Apparent age hardening appears at 873 K to 1173 K (600 °C to 900 °C), and no age softening occurs even after 1473 K (1200 °C) aging. The age hardening of this alloy is attributed to the transformation of the bcc phase to σ phase. Detailed variations of hardness and the microstructure of aged alloys are reported in this article.