Correlation between Microstructures and Oxidation Resistance in Zr-Nb-Ti Alloys

Oxidation behavior of Zr-10Nb-10Ti and Zr-10Nb-20Ti (compositions are in atomic percent) alloys has been investigated in air between 300 °C and 700 °C. Higher Ti content in the alloy enhances the oxidation resistance. The calculated isotherms by PANDAT[1,2] show that 20Ti enters a three-phase (αZr-hcp, βNb-bcc, and βZr-bcc) region at 500 °C, while 10Ti alloy continues to be a two-phase (αZr and βNb) alloy until 550 °C and then enters the three-phase (αZr, βNb, and βZr) region. Both alloys have a single-phase βZr solid solution at 700 °C, which is detrimental for the oxidation resistance. The βNb phase greatly contributes to the oxidation resistance in these two alloys. The common oxidation products have been identified as TiO₂, ZrO₂, and Nb₂O₅. Both alloys suffer from pest oxidation at temperatures between 500 °C and 550 °C, respectively (20Ti and 10Ti), up to 700 °C. X-ray diffraction (XRD) indicates strong peaks for monoclinic structure of ZrO₂ at temperatures above 600 °C.