Creep Life Prediction of Thermally Exposed Rene 80 Superalloy

verfasst von: M. Aghaie-Khafri, S. Farahany

Erschienen in: Journal of Materials Engineering and Performance | Ausgabe 7/2010

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The effects of long time thermal exposure on the microstructure and mechanical properties of Rene 80 superalloy were investigated by means of scanning electron microscopy and accelerated creep tests at 190 MPa and 980 °C. Results obtained showed that the rupture lives of pre-exposed samples decreased by increasing the exposure time or exposure temperature. In addition, as a new finding the concept of contour maps of the constant life and minimum creep rate were introduced. These maps were used to estimate the effect of exposure time and exposure temperature on the creep rupture life and minimum creep rate of thermally exposed samples.

Vorheriger Artikel Impact Energy of Functionally Graded Steels in Crack Arrester Configuration

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

T.M. Maccagno, A.K. Koul, J.P. Immarigeon, L. Cutler, R. Allem, and G. Lesperance, Microstructure, Creep Properties, and Rejuvenation of Service-exposed Alloy 713C Turbine Blades, Metall. Trans. A, 1990, 21, p 3115–3125CrossRef

J.A. Brown, R. Freer, and A.T. Rowley, Reconditioning of Gas Turbine Components by Heat Treatment, ASME J. Eng. Gas Turb. Power, 2001, 123, p 57–61CrossRef

R. Viswanathan, Damage Mechanisms and Life Assessment of High-Temperature Components, ASM International, Ohio, 1989

R. Orr, O.D. Sherby, and J.E. Dorn, Correlation of Rupture Data for Metals at Elevated Temperatures, Trans. ASME, 1954, 46, p 113–118

F.R. Larson and J. Miller, A Time-Temperature Relationship for Rupture and Creep Stress, Trans. ASME, 1952, 74, p 756–775

A.K. Koul and R. Castilo, Assessment of Service Induced Microstructural Damage and Its Rejuvenation in Turbine Blades, Metall. Trans. A, 1988, 19, p 2049–2066CrossRef

G. Marahleh, A.R.I. Kheder, and H.F. Hamad, Creep-Life Prediction of Service-Exposed Turbine Blades, Mater. Sci. Eng. A, 2006, 433, p 305–309CrossRef

F.C. Monkman and N.J. Grant, Proc. ASTM, 1956, 56, p 593–620

G.E. Fuchs, Solution Heat Treatment Response of a Third Generation Single Crystal Ni-Base Superalloy, Mater. Sci. Eng. A, 2003, 300, p 52–60

10.

J. Safary and S. Nategh, On the Heat Treatment of Rene-80 Nickel-Base Superalloy, J. Mater. Process. Technol., 2006, 176, p 240–250CrossRef

11.

C.T. Sims, N.S. Stoloff, and W.C. Hagel, Superalloys II, Wiley, New York, 1972, p 98–131

12.

J. Zrnik, P. Strunz, V. Vrchovinsky, O. Muransky, Z. Novyc, and A. Wiedenmann, Degradation of Creep Properties in a Long-Term Thermally Exposed Nickel Base Superalloy, Mater. Sci. Eng. A, 2004, 387–389, p 728–733

13.

E. Balikci, R.A. Mirshams, and A. Raman, Tensile Strengthening in the Nickel-Base Superalloy IN738LC, J. Mater. Eng. Perform., 2000, 9, p 324–329CrossRef

14.

I. Calliari, M. Magrini, and M. Dabalà, Microstructural Evolution of Udimet 720 Superalloy, J. Mater. Eng. Perform., 1999, 8, p 111–115CrossRef

15.

M. Lifshitz and V.V. Slyozov, The Kinetics of Precipitation from Supersaturated Solid Solution, J. Phys. Chem. Solids, 1961, 19, p 35–50CrossRefADS

16.

C. Wagner, Theorie der Alterung von Niederschlagen Durch Umlosen, Z. Electrochem., 1961, 65, p 581–591 (in German)

Titel: Creep Life Prediction of Thermally Exposed Rene 80 Superalloy
verfasst von: M. Aghaie-Khafri
S. Farahany
Publikationsdatum: 01.10.2010
Verlag: Springer US
Erschienen in: Journal of Materials Engineering and Performance / Ausgabe 7/2010
Print ISSN: 1059-9495
Elektronische ISSN: 1544-1024
DOI: https://doi.org/10.1007/s11665-009-9584-6

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 7/2010

Effect of Fly Ash Particles on the Compressive Properties of Closed-Cell Aluminum Foams

Effects of Thermal Cycling on the Temperature Memory Effect of TiNiNb Alloy

Effect of Surface Roughness on the Oxidation Behavior of the Ni-Base Superalloy ME3

Effects of Minor Sr on As-Cast Microstructure and Mechanical Properties of ZA84 Magnesium Alloy

Effects of Hydrogen on Ni47Ti44Nb9 Shape Memory Alloy

Wide Range Temperature Memory Effect of an In Situ NiTi Alloys Composite

Premium Partner

Marktübersichten