Crystallographic Orientation of the ε → α′ Martensitic (Athermal) Transformation in a FeMnAlSi Steel
Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 8/2014
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The presence of athermal ε- and α-martensite (α′) in the as-cast structure of a Fe-0.08C-1.95Si-15.1Mn-1.4Al-0.017N alloy has been revealed by electron backscattered diffraction analysis. The alloy exhibited two athermal martensitic transformations described by γ → α′ and γ → ε → α′. The Shoji–Nishiyama orientation relationship was observed between γ-austenite and ε-martensite, while α-martensite nucleated from γ-austenite exhibited a Kurdjumov–Sachs orientation relationship. Six crystallographic variants of α-martensite consisting of three twin-related variant pairs were observed in ε-bands. A planar parallelism of {0001}ε || {110}α′ and a directional relation of \( \left\langle {1\bar{1} 1} \right\rangle \alpha ' \) lying within 1 deg of \( \left\langle {\bar{1} 2\bar{1} 0} \right\rangle \varepsilon \) existed for these variants.