Effect of attrition milling on the piezoelectric properties of Bi_0.5Na_0.5TiO₃-based ceramics

Bismith sodium titanate (BNT)-based powders were prepared by conventionally mixed-oxide method using Bi₂O₃, Na₂CO₃ and TiO₂. The La₂O₃ was added as the modifier to the BNT composition for easily poling and reducing an abnormal dielectric loss at high temperatures. In this study, the investigated compositions were Bi_0.5Na_0.5TiO₃ and Bi_0.5Na_0.485La_0.005TiO₃. The powders were calcined at 900 °C for 2 h by slow heating rate at 100 °C/h. The calcined BNT-based powders were then attrition-milled for 3 h with a high speed at 350 rpm. After drying, the fine powders were uniaxially pressed and then cold-isostatically pressed (CIP) at 240 MPa for 10 min. All pressed pellets were sintered at 1000–1100 °C for 2 h in air atmosphere. The microstructure of sintered pellets was investigated by SEM. Results of dielectric and piezoelectric property measurement were also reported.