Effect of BiAlO₃ concentration on the dielectric and piezoelectric properties of lead-free (Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ piezoelectric ceramics

In this paper, lead-free (1-x)(Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃-xBiAlO₃ (BNBT-BA, x = 0, 0.010, 0.015, 0.020, 0.025, and 0.030) piezoelectric ceramics were synthesized using a conventional solid-state reaction method. The effect of BiAlO₃ concentration on dielectric, ferroelectric and piezoelectric properties were investigated. The ferroelectric and piezoelectric properties of BNBT ceramics are significantly influenced by the presence of BA. In the composition range studied, X-ray diffraction revealed a perovskite phase with the coexistence of rhombohedral and tetragonal phases. The temperature dependence of dielectric properties showed that the depolarization temperature (T _d) shifted towards lower temperatures and that the degree of diffuseness of the phase transition around T _d and T _m became more obvious with increasing BiAlO₃ content. The remanent polarization increased with increasing BA, and reached a maximum value of 30 μC/cm² at x = 0.020. As a result, at x = 0.020, the piezoelectric constant (d ₃₃) and the electromechanical coupling factor (k _p) of the ceramics attained maximum values of 188 pC/N and 34.4 %, respectively. These results indicate that BNBT-BA ceramics is a promising candidate for lead-free piezoelectric materials.