Effects of LiF addition on the sintering behavior and microwave dielectric properties of Li₂Mg₃SnO₆ ceramics

Li₂Mg₃SnO₆ (abbreviation for LMS) ceramics doped with 1–4 wt% lithium fluoride (LiF) were prepared by the conventional solid-state reaction method. The effects of LiF addition on the phase compositions, sintering behaviors and microwave dielectric properties of LMS ceramics were investigated. A small amount of LiF addition could effectively decrease the sintering temperatures due to the liquid phase in the sintering process and induced no apparent degradation of the microwave dielectric properties. The optimized quality factor values for each composition firstly increased and then decreased with the increase of the LiF content. Whereas, the optimized dielectric permittivity increased with increasing of the LiF content. Distinguished microwave dielectric properties with a dielectric constant (ε _r) of 11.13, a quality factor (Q·f) of 104,750 GHz, and a temperature coefficient of resonant frequency (τ _f ) of −10.83 ppm/°C were obtained for LMS ceramics sintered at 950 °C doped with 3 wt% LiF, which showed that the materials were suitable for the low temperature co-fired ceramics applications (LTCC).