Effects of PNN/PZT ratios on phase structure, electric properties and relaxation behavior of PZN–PNN–PZT ceramics
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 4/2016
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Pb(Zn1/3Ni2/3)c(Ni1/3Nb2/3)a(ZrxTiy)bO3 (PZN–PNN–PZT, the ratios of PNN/PZT a/b were 0.88, 1 and 1.136) piezoelectric ceramics were prepared by a traditional solid-state reaction method. The effects of PNN/PZT ratio on phase structure, microstructure and electric properties as well as the relaxation behaviors of PZN–PNN–PZT ceramics were investigated. The XRD patterns showed that all ceramics samples had a pure perovskite phase structure. Meanwhile, it was found that the phase structure undergoes a tetragonal, tetragonal-rhombohedral to rhombohedral transition as ratios of PNN/PZT increased. With the increasing of a/b from 0.88 to 1.136, the dielectric constant and diffusive phase coefficient decreases, it was indicated that relaxation behaviors also decreased. When ceramics with a/b was 1.136, the dielectric relaxation γ reached the minimum and electrical properties were poor. The electric properties of ceramics with a/b was 1.00 have an excellent properties, it was indicated that ceramics reached an optimization at the MPB structure.