Enhanced piezoelectricity and photoluminescence in Dy-modified 0.94(Bi1−x Dy x )0.5Na0.5TiO3–0.06BaTiO3 lead-free multifunctional ceramics
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 7/2015
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Lead-free 0.94(Bi1−x
Dy
x
)0.5Na0.5TiO3–0.06BaTiO3 ceramics were prepared by an ordinary sintering method and their piezoelectric and photoluminescent properties were studied. All the ceramics possess a pure perovskite structure with the coexistence of the rhombohedral and tetragonal phase. The partial substitution of Dy3+ for Bi3+ enhanced effectively the piezoelectricity of the materials. The optimum piezoelectricity is obtained at x = 0.025, giving d
33 = 190 pC/N and k
P = 37.2 %, respectively. After the addition of Dy3+, excellent photoluminescence of the ceramics is induced. The Dy-doped ceramics exhibit strong emissions at ~478 nm (blue) and ~575 nm (yellow), corresponding to 4F9/2 → 6H15/2 and 4F9/2 → 6H13/2 of Dy3+ transitions, respectively. The optimum photoluminescence of the ceramics is reached at x = 0.025. The ceramics with the doping of 2.5 mol% Dy3+ exhibit simultaneously good piezoelectricity, strong ferroelectricity and excellent photoluminescence, suggesting a promising application in the electro-optic devices.