Fabrication of high Tc lead free (1 − x)BaTiO3–xBi0.5K0.5TiO3 positive temperature coefficient of resistivity ceramics using reoxidation method
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 5/2011
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
(1 – x)BaTiO3−xBi0.5K0.5TiO3 (abbreviated as BT–BKT, where x = 0, 0.1 and 0.2) ceramics were prepared by solid state reaction method. All ceramic samples were sintered in a pure N2 flow atmosphere, subsequently reoxidized at a temperature range of 800–1,100 °C in air for several hours. The influences of BKT content and reoxidation on the positive temperature coefficient of resistivity (PTCR) behavior of ceramic samples were investigated. BT–BKT ceramic samples sintered in N2 possessed relatively low room temperature resistivity (ρRT) and showed weak PTC effect. Through an appropriate reoxidation, the ceramic samples re-obtained PTC effect of almost three orders of magnitude. With the addition of BKT, the Curie temperature (Tc) was enhanced by ~50 °C than the pure BT ceramics.