High dielectric tunability of ferroelectric (Ba1−x,Srx)(Zr0.1,Ti0.9)O3 ceramics
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 6/2014
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
(Ba1−x,Srx)(Zr0.1,Ti0.9)O3 (BSZT) ceramics with x = 0, 0.05, 0.15, 0.25, 0.35 and 0.45 were prepared by conventional solid state reaction method. The structural characterization with X-ray diffraction and scanning electron microscopy indicate a monotonical drop in lattice constants and grain size with the increase
of Sr concentration. Consequently, the Curie temperature and remnant polarization of the ceramics exhibit a strong compositional dependence. A linear relationship between the Curie temperature and Sr concentration is revealed. At x = 0.45, the BSZT ceramics show substantially high tunability of over 55 % under 20 kV/cm dc electric field with very low dielectric loss value of 0.0025 at room temperature, suggesting the BSZT ceramics could be a promising alternative to traditional (Ba,Sr) TiO3 ferroelectrics for developing high frequency tunable dielectric devices.