1 Introduction
In previous work, the temporary shear thinning behaviour of lubricant blends containing various commercial viscosity modifier additives (VMs) was measured over a wide shear rate range at several temperatures [1]. It was found that for all but one of the VMs, the viscosity of a given blend at all shear rates and temperatures could be described by a single equation based on time–temperature superposition. The resulting shear thinning equations were then used to explore the impact of the VMs on plain bearing friction using an isothermal, 3D hydrodynamic lubrication model [2]. This showed that VMs can reduce friction in two ways, by increasing viscosity index, leading to a low viscosity at low temperatures, and via shear thinning which reduces effective viscosity in high sliding speed, high shear rate lubricated contact conditions [2].
The current paper describes a combined experimental and modelling study of the impact of temporary shear thinning of VM blends on the friction of a plain journal bearing. A journal bearing machine (JBM) supplied by PCS Instruments, Acton, UK, is used to measure the hydrodynamic friction of a steadily loaded engine bearing, lubricated by some of the same VM blends characterised previously [1]. Friction is measured over a range of applied speeds, loads and oil supply temperatures.
Anzeige
In practice, plain journal bearings experience substantial thermal effects during operation so that their oil film temperature is usually considerably higher than the oil supply temperature, and it is essential to take this into account when interpreting bearing friction measurements. To address this, the temperature of the bearing is monitored using thermocouples. Alongside this, a 3D, thermal, hydrodynamic lubrication model of the bearing is employed to explore aspects of the thermal behaviour of the bearing not amenable to direct measurement. This allows JBM friction measurements to be compared with predicted friction for the VM blends studied, and thus to confirm experimentally the contribution of VMs to reducing hydrodynamic friction.
2 Background
Up to the mid-1970s, the temporary shear thinning behaviour of VM-containing engine oils was generally considered undesirable since it led to reduced hydrodynamic film thickness and thus the possibility of increased engine wear [3]. It was then noted that multigrade engine oils gave lower friction and thus better fuel economy than single grade oils of the same summer grade and that this arose at least in part from the shear thinning properties of VM polymer-containing oils [4]. In recent years, the ability of VMs to confer temporary shear thinning response and thus reduce hydrodynamic friction has become an important tool in the formulation of fuel-efficient engine oils [5, 6].
Until quite recently, one limitation in the study of the impact of temporary shear thinning on friction was that it was not possible to measure viscosities at shear rates above about 106 s−1, whereas the shear rates present in actual engine components can considerably exceed this value [7]. As demonstrated in a recent paper by the authors, this issue has now been addressed with the development of the ultrashear viscometer (USV) that is able to reach 107 s−1 without significant shear heating, enabling the development of reliable, isothermal viscosity-shear rate flow curves [1]. Using the USV, Warren et al. measured the viscosities of various model and formulated VM-containing oils up to high shear rate and compared these with film thickness and friction measurements in two journal bearing machines [8]. In most cases, the presence of shear thinning led to a reduction in friction compared to a base oil of comparable viscosity.
In principle, it should be straightforward to determine the impact of lubricant shear thinning on the friction of lubricated components such as plain bearings by solution of the relevant hydrodynamic lubrication equations in conjunction with a viscosity–shear rate relationship. However in practice, there are a number of problems. As well as the difficulty of measuring viscosity at very high shear rates, a major issue is that considerable energy dissipation due to fluid film shear occurs in plain journal bearings. This means that hydrodynamic analysis should incorporate both shear thinning and thermal effects and this requires a mathematical description of the dependence of lubricant viscosity on both shear rate and temperature, as well as a thermal model of the whole bearing. Another problem is the possibility, especially with low viscosity lubricants, of components operating in mixed lubrication, with a significant friction contribution from asperity contact. Yet another issue, which will be discussed later in this paper, concerns the extent to which the lubricant fills the bearing gap in the inactive, ambient pressure zone.
Anzeige
A number of studies have attempted to address some of the above issues. Taylor has measured the shear thinning curves of two formulated engine oils and employed fitted Cross shear thinning equations to explore the impact of shear thinning on friction using an isoviscous, short bearing model [7]. Ferron et al. have modelled the full thermal behaviour of hydrodynamic bearings to explore the impact of shear heating and lubricant viscosity on bearing temperature and eccentricity [9]. In a series of papers, Allmaier et al. studied engine journal bearing lubrication by combining experimental measurements of friction and bearing temperature with hydrodynamic models [10‐14]. Initial work employed VM-free oils but recently work on a formulated shear thinning oil has been reported [15]. This showed that it was essential to incorporate shear thinning effects to reliably predict friction performance. Unfortunately, the shear thinning measurements on which the study was based were obtained using a quartz crystal viscometer and it is questionable whether such measurements are comparable to viscosity measured in high shear systems.
This paper describes a study of the impact of lubricant shear thinning on bearing friction using a combined experimental and modelling approach. It is based on VM-containing lubricants whose shear thinning properties were fully characterised in [1]. After describing the experimental and modelling methods, results are presented in two sections. The first measures the friction of the bearing lubricated with a Newtonian oil and compares this with predicted friction in order to validate the approach. Interpretation is informed using a full thermo-hydrodynamic model. Then a series of VM-containing oils are studied in order to measure the impact of shear thinning on friction.
3 Test Oils and Viscometrics
In previous work, the authors investigated the temporary shear thinning properties of a base oil and a series of VM blends, all having the same HTHS viscosity of 3.7 mPa s (at 106 s−1, 150 °C) [1]. In the current work, a subset of these oils is studied, as listed in Table 1. The original oil codes used in [1, 2] have been retained. Oils #1, #4, #5, #7, and #10 are simple solutions of different VMs in the same 6 cSt KinVis Group II base oil. Oil #11 has the same base oil but contains both a VM and a detergent-inhibitor package. Oil #18 is a mixture of PAOs blended to have an HTHS of 3.7 mPa s and thus serves as a Newtonian reference oil.
Table 1
VM-containing oils (#1–#17) and the reference oil (#18) studied
Oil | VM type | VM wt% | DI pack | DI pack wt% | KV100C (cSt) | VI | Base oil type | HTHS (mPa s) |
|---|---|---|---|---|---|---|---|---|
#1 | SIP1 | 11.5 | – | – | 16.19 | 162 | G-II | 3.73 |
#4 | SIP2 | 25.0 | – | – | 19.91 | 183 | G-II | 3.70 |
#5 | A-OCP | 11.5 | – | – | 13.60 | 153 | G-II | 3.69 |
#7 | D-PMA | 9.0 | – | – | 12.54 | 191 | G-II | 3.70 |
#10 | PMA | 13.5 | – | – | 11.40 | 276 | G-II | 3.77 |
#11 | SIP3 | 15.7 | D1 | 11.9 | 13.73 | 178 | G-II | 3.73 |
#18 | None | – | – | – | 12.48 | 148 | G-IV | 3.70 |
Further information on these oils can be found in [1].
The dynamic viscosity of all the above oils was measured over a wide shear rate range up to 107 s−1 as described in [1], and it was found that their viscosity versus shear rate behaviour at a given temperature could be described by the Carreau–Yasuda equation [16]:
$$\eta ={\eta _\infty }+\left( {{\eta _{\text{o}}} - {\eta _\infty }} \right){\left( {1+{{\left( {A\dot {\gamma }} \right)}^a}} \right)^{\left( {\frac{{n - 1}}{a}} \right)}},$$
(1)
where η is the dynamic viscosity of the fluid at shear rate \(\dot {\gamma }\); ηo is the first Newtonian viscosity; \({\eta _\infty }\) is the second Newtonian viscosity (approximated to the viscosity of the blend’s base oil) and A; n and a are constants of fit.
It was also found that for all except oil #10, the shear thinning curves at different temperatures could be collapsed onto a single curve by using time temperature superposition in which the shear rate is multiplied by a shift factor aT, to give a reduced shear rate, \({\dot {\gamma }_{\text{r}}}={a_{\text{T}}}\dot {\gamma }\). The shift factor aT is a shift from a reference temperature, TR, (60 °C in this study) at which aT is taken to be unity, and is defined by Eq. 2 [17].
$${a_{\text{T}}}=\frac{{{{\left[ {{\eta _{\text{o}}} - {\eta _\infty }} \right]}_{(T)}}}}{{{{\left[ {{\eta _{\text{o}}} - {\eta _\infty }} \right]}_{\left( {{T_{\text{R}}}} \right)}}}}.\frac{{{T_{\text{R}}}}}{T}$$
(2)
This allows a single reduced Carreau–Yasuda equation to be developed to describe how viscosity varies with both shear rate and temperature for a given VM blend:
$$\eta ={\eta _\infty }+\left( {{\eta _{\text{o}}} - {\eta _\infty }} \right){\left( {1+{{\left( {{A_{\text{r}}}{a_{\text{T}}}\dot {\gamma }} \right)}^{{a_{\text{r}}}}}} \right)^{\left( {\frac{{{n_{\text{r}}} - 1}}{{{a_{\text{r}}}}}} \right)}},$$
(3)
where the three constants Ar, nr and ar are now best fits to the measured viscosity values of the blend at all shear rates and temperatures [1].
The above means that viscosity of a VM blend can be calculated at any shear rate and temperature of interest so long as (i) the reduced Carreau Yasuda contacts Ar, nr and ar are known for the blend and (ii) the low shear rate viscosities ηo and \({\eta _\infty }\) are known or can be calculated at the temperature of interest and at the reference temperature.
Table 2 lists the reduced Carreau Yasuda constants of the VM blends studied in this work. As discussed in [1], oil #10 did not show satisfactory time temperature superposition collapse using the shift factor expression in Eq. 2. This was addressed by allowing aT for this oil to vary with temperature empirically, based on experimental measurements at different temperatures. For oil #10, viscosity can be thus predicted by using the Carreau–Yasuda constants in Table 2, but multiplying the value of aT calculated from Eq. 2 by the factor 1, 1.3, 3.2, 3.7, 3.7 at 60 °C, 80 °C, 100 °C, 120 °C and 150 °C, respectively, and allowing this factor to vary linearly with temperature between these bounding values at intermediate temperatures.
Table 2
Reduced Carreau–Yasuda constants for VM blends (reference temperature TR = 60 °C)
Test oil |
A
r (µs) |
n
r
|
a
r
|
|---|---|---|---|
#1 | 21.88 | 0.36 | 1.00 |
#4 | 68.39 | 0.47 | 1.00 |
#5 | 18.41 | 0.66 | 1.52 |
#7 | 21.13 | 0.75 | 2.26 |
#10 | 1.70 | 0.69 | 1.60 |
#11 | 39.36 | 0.75 | 2.50 |
The required values of low shear rate viscosities ηo and \({\eta _\infty }\) at both the temperature of interest and the reference temperature of 60 °C can be straightforwardly calculated from the Vogel viscosity-temperature equation, Eq. 4, using the Vogel fit constants for each fluid and its base fluid as listed in Table 3.
Table 3
Low shear rate Vogel constants of VM blends and component base oils
Test oil | Vogel constants of test oil (to determine ηo) | Vogel constants of corresponding base oil (to determine \({\eta _\infty }\)) | ||||
|---|---|---|---|---|---|---|
Vogel ao (mPa s) | Vogel bo (°C) | Vogel co (°C) | Vogel ao (mPa s) | Vogel bo (°C) | Vogel co (°C) | |
#1 | 0.11158 | 989.308 | − 107.84 | 0.06322 | 883.001 | − 103.24 |
#4 | 0.12945 | 1028.18 | − 113.64 | ““ | ““ | ““ |
#5 | 0.0844 | 1024.21 | − 110.63 | ““ | ““ | ““ |
#7 | 0.161106 | 850.124 | − 105.28 | ““ | ““ | ““ |
#10 | 1.13028 | 310.73 | − 50.628 | ““ | ““ | ““ |
#11 | 0.19964 | 770.535 | − 92.505 | ““ | ““ | ““ |
#18 | 0.04839 | 1193.38 | − 124.72 | – | – | – |
$${\eta _o}={a_0}{e^{{b_{\text{o}}}/\left( {T - {c_{\text{o}}}} \right)}}$$
(4)
To illustrate the data on which this study is based, Fig. 1a shows the individual viscosity measurements for oil #5 plotted against the reduced shear rate at four temperatures, together with the line fit by Eq. 3. The ordinate of this graph is the normalised viscosity or shear stability index (SSI) defined as
Fig. 1
a Measured SSI versus reduced strain rate and Carreau–Yasuda best fit for oil #5. b Measured low shear rate viscosity versus temperature and Vogel equation best fits for oil #5 and base oil used in the VM blends
$${\text{SSI}}=\frac{{\left( {\eta - {\eta _\infty }} \right)}}{{\left( {{\eta _{\text{o}}} - {\eta _\infty }} \right)}}.$$
(5)
×
![]()
Figure 1b shows low shear rate measurements and Vogel best fits for oil #5 and also the base oil used in the VM blends.
4 Method: Journal Bearing Machine (JBM)
Friction tests were carried out using a Journal Bearing Machine (JBM), PCS Instruments, Acton, UK. The rig consists of a lined steel shaft that rotates inside a commercial engine bearing shell, made up of two half-shells housed in a modified connecting rod. It is shown in Fig. 2.
Fig. 2
Photograph of JBM
×
![]()
Load is applied to the bearing via a lever arm and can either be a steady load or a transient one in which an additional load is applied on top of a continuous one using a rotating cam, as shown in Fig. 3. In the current study, steady load conditions were used. The load is transferred via a coupling from which both the load and friction can be measured with strain gauge load cells. In practice, this set-up provides almost but not quite perfect isolation of the normal applied force (load) from the lateral force (torque and thus friction), so that a small proportion of the load appears in the friction measurement. Because the friction coefficient is only ca 0.001–0.01, this load contribution is significant. In order to eliminate it, two measurements are averaged with the shaft rotating in opposite directions, which has the effect of cancelling the load contribution from the friction measurement.
Fig. 3
Schematic of loading system
×
![]()
In the current study, commercial Chrysler plain bearings (3.6 L, V6 engine) were used, of length L = 17.8 mm with shaft diameter, D = 59.5 mm. The radial clearance was 29 µm. Tests were carried out at eight rotational speeds ranging from 1000 to 3500 rpm, three loads in the range 1–3 kN (corresponding to bearing pressures of 1–3 MPa) and oil supply temperatures of 60, 80, 100 and 120 °C. Oil was supplied at 150 kPa pressure. A new pair of bearing half-shells from a single batch was used for each test oil. This was run in with the test oil over a series of decreasing loads, 10 kN, 7 kN, 5 kN, 3 kN. At each run-in load stage, the shaft was rotated in both directions at each of the eight test speeds.
Although oil is supplied at a controlled temperature, it is important when analysing plain journal bearing performance to appreciate that the actual oil film temperature can be quite different from the oil supply temperature. At 3000 rpm and 3 kN load, the power loss in the bearing was typically 100 W in this study and this resulted in a rapid rise in bearing temperature. The final, steady-state oil film temperature depends on the heat transfer properties of the bearing and its holder as well as on the oil supply temperature.
In order to monitor temperature and explore the thermal properties of the bearing, thermocouples were used in the JBM as illustrated in Fig. 3. Thermocouple A (TC A) is mounted between the bearing shell and the connecting rod housing at 90° from the applied load position. When the shaft rotates in a clockwise direction, the minimum film thickness moves round the bearing so that thermocouple A is in the cavitating zone at a bearing angle of 270°−ψ, where ψ is the attitude angle, as shown in Fig. 19a in the Appendix. Thermocouple B (TC B) is located between piston rod and the loading system. A third thermocouple is placed in the test chamber close to the connecting rod to monitor the ambient temperature experienced by the latter’s outer surface. The fourth thermocouple measures the oil supply temperature and uses this via a feedback loop to stabilise this at a set value.
The experimental test protocol was as follows:
(i)
The test rig was cleaned and flushed eight times with 300 ml of test oil before being filled with 500 ml of test oil.
(ii)
Oil supply temperatures of 120 °C, 100 °C, 80 °C, 60 °C were studied in succession.
(iii)
For each oil supply temperature, the oil was circulated while running the bearing at 3000 rpm and 3 kN load until both the set oil supply temperature and the bearing temperature (measured by thermocouple A) stabilised. This generally took about 10–20 min.
(iv)
Friction was then measured at a series of applied loads and speeds.
It should be noted that because two friction measurements were made, with the shaft rotating in opposite directions, thermocouple A switched positions from being in the cavitation region (at about 230°) to the active converging zone (at about 50°) as the shaft changed direction. This provided two measurements of temperature around the bearing. In this paper, only the measurement made in the cavitation region is utilised.
5 Shear Thinning Thermohydrodynamic Bearing Model
A finite difference-based 3D thermal model was used to analyse the hydrodynamic and heat transfer behaviour of the lubricated bearing. This is based on iterative solution of (i) a 3D generalised Reynolds equation to determine flow and pressure in the oil film, (ii) the reduced Carreau Yasuda equation to determine viscosity at local shear rate and temperature, (iii) the energy equation to determine the temperature distribution in the oil film and (iv) the Laplace equation to determine the heat flux through the bearing shell and connecting rod holder. Further details of this model are provided in “Appendix”.
It is important to note that this model was not intended to simulate precisely the bearing under study, which would have required inclusion of the complex geometry of the connecting rod, as well as accurate thermal properties of all of the materials and measurement of the heat transfer properties of the relevant surfaces. Such simulation is feasible but was not within the scope of the study. Instead the model was based on an idealised cylindrical bearing geometry with representative heat transfer constants and was intended primarily to inform on the general distribution of temperature in the bearing system and, as outlined in Sect. 6 below, to justify the use of an isothermal model based on an effective oil film temperature. However, it also provided a way to compare directly the impact of different VMs in a thermo-hydrodynamic bearing.
6 JBM Study Using Newtonian Oils
Initial work was carried out with the Newtonian base oil #18 to develop a test methodology for taking account of bearing temperature. Figure 4 shows how friction varied with shaft speed at three loads and a fixed oil supply temperature. As expected, friction increases with speed and load. Tests also showed that friction reduced with increasing oil supply temperature at a given load and speed and was relatively insensitive to variations of load at fixed speed and oil supply temperature.
Fig. 4
Influence of sliding speed on friction for oil #18 at 3 loads and 120°C
×
![]()
Figure 5 shows all the friction measurements made (at 3 loads and 8 speeds at 80 °C, 100 °C and 120 °C and one load and 8 speeds at 60 °C) in classical Stribeck form of friction coefficient versus usηsupply/W, where us is the shaft surface speed, W is the applied load and ηsupply is the viscosity at the oil supply temperature. The measurements fall on separate curves, with friction coefficient values obtained at higher oil supply temperatures being greater than those measured at lower temperatures.
Fig. 5
Friction coefficient versus usηsupply/W for oil #18 at all loads and speeds
×
![]()
Figure 6 shows the same friction coefficient data plotted against the Stribeck number usηeff/W where ηeff is now the viscosity of the oil at the temperature measured by thermocouple A, between the bearing shell and its holder in the cavitation zone. This has the effect of collapsing the data onto a single curve, as expected from isothermal journal bearing theory. It confirms the importance of taking account of thermal effects when interpreting and predicting friction in journal bearing lubrication.
Fig. 6
Friction coefficient versus usηeff/W for oil #18 at all loads and speeds; ηeff is the viscosity at temperature measured by thermocouple A during each test
×
![]()
The thermo-hydrodynamic model was used to determine the temperature distribution in the lubricated bearing. This is illustrated in Figs. 7 and 8 for a bearing operating with oil #18 at 3000 rpm, 2 kN and 80 °C oil supply temperature. Figure 7 shows how the predicted mid-oil film temperature varies round the bearing. The oil film heats up in the converging region and then stabilises over most of the high pressure and cavitation zone at a value of between 95 and 96 °C. It then falls sharply as fresh oil at 80 °C is supplied to fill the gap. Since the eccentricity ratio is ca. 0.75, only about 15% of the originally supplied oil passes through the minimum film thickness, so 85% is supplied as fresh oil at 80 °C. Of note is the fact that the bearing temperature is quite constant over most of the load supporting region. This is primarily because the shaft temperature is constant in the circumferential direction, which imposes a stabilising boundary condition on the oil film.
Fig. 7
Predicted variation of mid-oil film temperature around bearing lubricated by base oil #18 at 3000 rpm, 2 kN load and oil supply temperature 80 °C
×
![]()
Fig. 8
Predicted variation of temperature through the oil film and the sleeve/connecting rod at bearing angle 235° and y = 0. Bearing lubricated by base oil #18 and operating at 3000 rpm, 2 kN load and oil supply temperature 80 °C, ambient temperature 70 °C. Location of thermocouple A shown
×
![]()
Figure 8 shows how the predicted temperature varies through the oil film at one location of the bearing (mid line in the axial direction, and 235° around the bearing and thus in the cavitation zone very close to thermocouple A). The temperature profiles through both an oil film streamer and the bearing/connecting rod are shown (the depth scales are of course quite different for the two). This plot shows that the thermocouple A located just below the shell will measure a temperature slightly lower that the oil/bearing interface temperature and that the temperature variation across the bearing is small, as expected since the oil film is thin.
Because most of the thin film region of the bearing, where the bulk of the friction originates, is at quite constant temperature, it is possible to use an isothermal solution to determine bearing friction, based on a single “effective temperature” and thus an effective oil viscosity. Such an isothermal, effective viscosity approach has been quite widely applied in bearing design [18, 19] and Allmaier suggested a weighted average temperature from four thermocouples distributed around a bearing to determine the effective bearing temperature [13]. To test the validity of the isothermal approximation for the current study, the thermo-hydrodynamic model was used to determine the bearing temperature distribution and friction over a wide range of conditions (1000–3500 rpm, 1 to 4 kN and 60 to 120 °C supply temperature) for both the reference oil #18 and a shear thinning oil #1. The predicted friction was then compared with the friction calculated using an isothermal model based on individual temperatures determined at various locations in the bearing from the full thermo-hydrodynamic model. It was found that the bearing temperature at the location of thermocouple A (i.e. 1. 4 mm below the oil/sleeve interface at a bearing angle of 270°-ψ) employed in an isothermal solution gave a friction prediction within 0.5% of that from the full thermo-hydrodynamic solution for all conditions and oils tested.
Figure 9 shows the predicted bearing friction from the isothermal hydrodynamic model using the temperatures measured with thermocouple A plotted against the measured friction for all the measured friction values for Oil #18. Two sets of predicted friction values are shown, one assuming a full set of cavitation streamers as discussed in the Appendix and the other assuming absence of cavitation streamers. There is good agreement between measured friction and friction predicted assuming the presence of cavitation streamers. These both validate the JBM measurements and also provide supportive evidence for the occurrence (and importance to friction) of cavitation streamers. At high friction, which corresponds to high-speed conditions, the measured friction falls slightly below the predicted friction. This is probably due to the inlet meniscus moving slightly upstream and/or some break-up of the cavitation streamers.
Fig. 9
Plot of predicted versus measured friction for all measured data. Predicted friction is calculated assuming the bearing is isothermal at the temperature measured by thermocouple A
×
![]()
The above work using a Newtonian reference oil shows that bearing friction can be measured accurately using the JBM and also predicted using an isothermal approach based on an effective oil film temperature. Similar measurements and analysis were made on the relatively low viscosity base oil used in the VM-containing oils #1–#11 and showed equally good agreement between measurement and prediction. This indicates that there is negligible contribution from boundary friction, which is perhaps unsurprising since the predicted minimum film thickness formed by this base oil (at 750 rpm, 3 kN load and 120 °C) was 1.2 µm, while the bearing roughness was less than 600 nm Rq.
7 JBM Study Using VM-Containing Oils
Friction and bearing temperature were measured for the VM-containing oils over the same range of conditions as the reference oil. However, direct quantification of the impact of VMs on journal bearing friction is not straightforward since friction and temperature are coupled and both vary from test to test. Nor was it possible to ensure that the bearing always reached full thermal equilibrium. Friction values measured at the same speed and load for different oils are thus not directly comparable.
One approach is to use the measured temperature at thermocouple A as an effective oil film temperature, as outlined in the previous section, and use this to determine the effective low shear rate viscosity of the test oil at that temperature. Friction coefficient can then be plotted against usηeff/W where ηeff is the effective viscosity at the mean bearing temperature. This is shown for oils #1 and #4 in Fig. 10a, b. The best fit line to data of friction versus usηeff/W for reference oil #18 (from Fig. 6) is shown as a dashed line. It is clear that the VM-containing oils give considerably lower friction than the VM-free oil in these Stribeck-type plots. However, unlike the reference oil, the data do not collapse on to a single line but vary systematically with bearing speed. This is because the oils’ effective viscosities reduce with increasing shear rate and thus sliding speed.
Fig. 10
Plots of measured friction coefficient versus the Stribeck number usηeff/W where ηeff is the low shear rate viscosity of the oil at the effective bearing temperature for all tests on a oil #1 and b oil #4
×
![]()
Figure 11 compares the bearing friction of all the test oils at usηeff/W = 0.0001 at 3000 rpm based on best fits through all of the measured data at this bearing speed. This shows clearly that all six of the VM-containing oils in a 6 cSt base oil show considerably lower friction than the reference oil.
Fig. 11
Friction coefficient at usηeff/W = 0.0001 m−1 based on measured data at a bearing speed of 3000 rpm
×
![]()
More detailed comparison of the various VM blends could only be made using the full thermo-hydrodynamic model to compare bearing temperature and friction for different blends at the same load, speed and oil supply temperature.
Figures 12, 13, 14 show the predicted maximum temperature reached in the oil film, the friction coefficient and the minimum film thickness respectively for all the oils at 3000 rpm, 2 kN load and an oil supply temperature of 80 °C.
Fig. 12
Maximum oil film temperature at 3000 rpm, 2 kN load, 80 °C oil supply temperature; from thermo-hydrodynamic model
×
![]()
Fig. 13
Calculated friction coefficient at 3000 rpm, 2 kN load, 80 °C oil supply temperature; from thermo-hydrodynamic model
×
![]()
Fig. 14
Calculated minimum film thickness at 3000 rpm, 2 kN load, 80 °C oil supply temperature; from thermo-hydrodynamic model
×
![]()
It is evident that all the VM-containing oils show both lower friction and consequently lower oil film temperature than the Newtonian reference oil, despite the latter having a smaller low shear rate viscosity. The VM-containing oils operate typically 2 to 4 °C lower than the reference oil and show between 10 and 15% lower friction. Film thicknesses of the VM-containing oils are also about 10–15% lower than the reference oil. Oils #1, #4 and #10 show the lowest friction.
Figure 15 shows how predicted bearing friction varies with oil supply temperature for all of the test oils at 3000 rpm and 2 kN load. Friction drops rapidly with oil supply temperature (and thus bearing temperature) for all oils, with oils #1, #4 and #10 showing the lowest friction in accord with Fig. 13. It should be noted that the friction values are not produced by oil films at the supply temperature shown, but at the considerably higher temperatures reached within the bearing. These are typically 80 °C, 95 °C, 110 °C and 130 °C at 60 °C, 80 °C, 100 °C and 120 °C oil supply temperature, respectively.
Fig. 15
Variation of calculated friction with oil supply temperature at 3000 rpm, 2 kN load; from thermo-hydrodynamic model
×
![]()
8 Discussion
The aim of this study was to explore the impact of viscosity modifier additives on friction in an engine bearing. However, bearing temperature rise plays a key role in controlling friction which means that, while tests can be carried out at a fixed oil supply temperature, it is not possible to conduct them at a controlled oil film temperature since oil film temperature and friction are coupled. Three essential components of the current work were therefore (i) the availability of a single equation for each VM blend (Eq. 3) that describes the dependence of viscosity on both shear rate and temperature; (ii) a bearing rig in which both friction and temperature can be measured; and (iii) a hydrodynamic model incorporating thermal and shear thinning behaviour.
In practice, it was not practicable to measure temperature of the actual oil film within the bearing, but the thermo-hydrodynamic model shows that bearing friction can be predicted reliably based on an isothermal hydrodynamic model using a single temperature measurement from between the bearing shell and its holder in the cavitation zone. Based on this measured temperature, close fit between measured and predicted friction was obtained, as shown in Fig. 9. Interestingly, the friction values measured appear to support the presence within the bearing of a full set of cavitation streamers under most conditions. Figure 16 shows similar graphs of friction predicted from the isothermal model based on thermocouple A plotted against measured friction for the VM-containing oils #1 and #10. These show close agreement at low bearing speeds but, as also seen with oil #18, lower than predicted friction at high speeds. Again this may be due to movement of the inlet meniscus and/or some breakdown of cavitation streamers.
Fig. 16
Plot of predicted versus measured friction for all measured data for two VM-containing oils. Predicted friction is calculated assuming the bearing is isothermal at the temperature measured by thermocouple A
×
![]()
Figure 13 compares the predicted friction coefficients of the test oils at a fixed load, speed and supply temperature, and shows that the VM-containing oils give lower friction that the reference oil. It is important to recognise that this reduction in friction reflects, quite simply, a lower effective viscosity at the prevailing temperature and shear rate conditions in the oil film and that there are two factors that contribute to this low viscosity; (i) low shear rate viscosity and (ii) shear thinning. These two factors explain the considerable difference in friction reduction of the test oils shown between Figs. 11 and 13. Figure 13 shows friction predicted from the thermo-hydrodynamic model, where both variations of low shear rate viscosity and shear thinning within the bearing are taken into account when calculating friction. However in Fig. 11, which incorporates the low shear rate viscosity of the oil at the bearing temperature, ηeff, in the Stribeck number, only the residual effect of shear thinning is shown.
Using the thermo-hydrodynamic model, it is straightforward to explore the impact of shear thinning on friction by comparing solutions in which shear thinning takes place with those when the same oil is not allowed to shear thin. This impact is defined as
$${\text{Friction~reduction~due~to~shear~thinning~}}\% =\frac{{{F_{{\text{Newtonian}}}} - {F_{{\text{shear~thinning}}}}}}{{{F_{{\text{Newtonian}}}}}}x100.$$
(6)
Figure 17 shows the percentage friction reduction for the VM blends resulting from shear thinning, as predicted from the thermo-hydrodynamic model.
Fig. 17
Percentage friction reduction due to shear thinning at 3000 rpm, 2 kN load, 80 °C oil supply temperature; from thermo-hydrodynamic model
×
![]()
This matches Fig. 11 quite closely and shows that oils #1 and #4 provide a large friction reduction due to shear thinning while oil #10 shows minimal such friction reduction. Oil #10 shows very little shear thinning because, as discussed in [1], it has relatively little thickening power below 100 °C and also it only shear thins significantly at very high shear rates.
Figure 18 compares the low shear rate viscosities of the test oils at the maximum prevailing oil film temperatures shown in Fig. 12. As might be expected these values parallel quite closely the KV100 values listed in Table 1. Oils #1 and #4 have relatively high low shear rate viscosities and these negate to some extent the contribution of shear thinning to their friction reduction. Oil #10, because of its extremely high VI, has relatively low viscosity at the bearing temperature, which more than compensates for its minimal shear thinning.
Fig. 18
Low shear rate viscosities of the test oils at their maximum oil film temperatures (shown in Fig. 12) at 3000 rpm, 2 kN load, 80 °C oil supply temperature; from thermo-hydrodynamic model
×
![]()
Fig. 19
a Bearing configuration under load and b unwrapped bearing and coordinate system. Gap shape is \(h=c(1+\varepsilon \cos \theta )\), \({\text{d}}h= - \;c\varepsilon \sin \theta {\text{d}}\theta\), \(x=R\theta\)
×
![]()
Fig. 20
Schematic diagram of regions of bearing that are full of oil
×
![]()
The actual bearing friction shown in Fig. 13 results from a combination of the two factors shown in Figs. 17 and 18, shear thinning and low shear rate viscosity and, since these appear to be inversely correlated, mean that all of the VM oils produced quite similar friction values. Another factor driving this similarity is thermal feedback, where oils that give low friction produce less shear heating, so their bearings run slightly cooler, which results in a higher viscosity and thus higher friction. This feedback process reduces the differences in friction between the oils in a thermo-hydrodynamic bearing but in practice has a relatively minor effect compared to the factors illustrated in Figs. 17 and 18.
It is of interest to consider why the magnitude of shear thinning and low shear rate viscosity are inversely correlated for the VM-containing oils studied. This is simply because all the test oils were formulated to have the same value of 3.7 mPa s HTHS. To achieve this value at 106 s−1 and 150 °C, those oils that shear thin strongly require higher values of low shear rate viscosity than those that shear thin relatively little.
Although this constraint imposes limits to how widely the friction properties of the VM-containing oils studied here can vary, the differences shown in Fig. 13 are still significant, with oils #1 and #10 giving 8–9% lower friction than oils #5 and #11. Without this constraint of requiring the same HTHS, it should be evident that for an oil to give low friction in an engine bearing it should combine low viscosity at low shear rate, a very high VI (so as to maintain low viscosity down to low temperatures) and a large amount of shear thinning at high bearing speeds.
9 Conclusions
This study has demonstrated the effectiveness of the JBM for studying the hydrodynamic friction properties of engine lubricants. It has also highlighted the importance of measuring or calculating actual bearing temperature in order to interpret friction results, since these temperatures are often quite different from oil supply temperatures.
Engine friction increases rapidly with increasing shaft speed but relatively slowly with increasing load.
It has been found, both experimentally and by comparison with the predictions of a thermo-hydrodynamic bearing model that an isothermal model incorporating shear thinning at an effective bearing temperature can be used to reliably predict bearing friction. The effective temperature is very close to the value measured using a thermocouple between sleeve and holder at a bearing angle of 270° in the stationary, loaded bearing; (270°-ψ when the shaft rotates).
The coupling of friction and temperature makes it difficult to compare quantitatively the impact of VMs on friction in the JBM since tests cannot be easily performed at the same effective bearing temperature. However, a thermo-hydrodynamic model incorporating shear thinning can be used to explore different VM blends. This is only possible because of (i) the availability of reliable measurements of viscosity up to 107 s−1 and (ii) the recent development of equations that describe the dependence of lubricant viscosity on both shear rate and temperature. It shows that there are two main factors that can contribute to low friction in engine bearings; (i) low viscosity at low shear rate over the whole bearing temperature range of interest, which can be enabled a low viscosity base oil and a high VI and (ii) the ability to shear thin at the high shear rate conditions present in engine bearings.
Acknowledgements
The authors would like to thank Repsol S.A. for supporting this work and supplying base fluids and additives.
Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.