Improved soft magnetic properties of Fe83.5Si7.5B5Cr4 amorphous nanocrystalline powder cores by adding Permalloy
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 22/2018
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
In this paper, the effect of adding Permalloy (< 15 µm) on Fe83.5Si7.5B5Cr4 amorphous nanocrystalline magnetic powder (< 50 µm) was studied. The best stress relief annealing temperature were revealed at the same time. The results showed that the addition of Permalloy will significantly affect the soft magnetic properties of Fe-based amorphous nanocrystalline powders. Compared to the Fe83.5Si7.5B5Cr4 amorphous nanocrystalline powder, the saturation magnetization of composite powders obviously increased (by 9.8–17.1%). When Permalloy content was 15 wt%, the sample had the highest effective permeability, which increased by 21.6% (f = 200 kHz). At the same time, the core loss was also reduced by 5.3% (Bm = 40 mT, f = 200 kHz) when Permalloy content was 10 wt.%. In addition, the magnetic powder core had the highest effective permeability and the lowest core loss when the stress relief annealing temperature was set to 773 K.