Influence of Thermomechanical Control Process on the Evolution of Austenite Grain Size in a Low-Carbon Nb-Ti-Bearing Bainitic Steel

On the basis of hot rolling practice, the effects of thermomechanical control process parameters on the evolution of austenite grain size before the deformation at non-recrystallization zone were investigated in detail. The inflections in the strain hardening rate versus true stress curves show that the dynamic recrystallization (DRX) has initiated for different deformation conditions studied in the present work. But the volume fractions of the equiaxed grains in the specimens which were immediately water quenched to room temperature after deformation are different from each other. Moreover, the main refinement mechanisms for different deformation conditions have been differentiated. It is interesting to note that the austenite grain size can be refined significantly with increasing the strain from 0.0 to 0.5 for different deformation temperatures. However, when the strain increases to 0.8, the austenite grain size cannot be further refined for the higher deformation temperature range, while the austenite grain size can be further refined for the lower deformation temperature range. In addition, the effect of strain rate on the austenite grain refinement is vigorous for the higher deformation temperatures. Moreover, the empirical equation to estimate the austenite grain size for different deformation parameters was established.