Preparation and characterization of high T c (1−x) BiScO3xPbTiO3 ceramics from high energy ball milling process

verfasst von: Lin Zhang, Zhuo Xu, Zhenrong Li, Song Xia, Xi Yao

Erschienen in: Journal of Electroceramics | Ausgabe 1-4/2008

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

(1-x)BiScO3xPbTiO3 powders were synthesized from a mixture of the oxides Bi2O3, Sc2O3, PbO and TiO2 using a Fritsch P4™ vario-planetary ball milling systems. The pure perovskite structure of BS-PT powder can well be obtained and the crystallite size of the powders was greatly reduced to 18–25 nm after milling 4 h. The rhombohedral–tetragonal phase boundary was observed for the ceramics sintered at 1,000–1,100 °C when x was around 0.64 and 3–7 μm grain size was obtained, which is smaller than traditional method. High Curie temperature (T c) and high dielectric constant can be obtained at the morphotropic phase boundary (MPB). As PbTiO3 contents increased from 60 to 68 mol%, the Curie temperature T c shifted toward higher temperature and the maximum dielectric constant increased. The experimental results demonstrate that the high-energy ball milling process is a promising method to prepare BS-PT materials.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat B. Jaffe, W.R. Cook, H. Jaffe, Piezoelectric Ceramics (Academic Press, Reported by R. A. N. Publishers. Marietta. Ohio. 1971) B. Jaffe, W.R. Cook, H. Jaffe, Piezoelectric Ceramics (Academic Press, Reported by R. A. N. Publishers. Marietta. Ohio. 1971)
2.
Zurück zum Zitat R.E. Eitel, C.A. Randall, T.R. Shrout, S.E. Park, P. Rehrig, Jpn. J. Appl. Phys. 41, 2099 (2002)CrossRefADS R.E. Eitel, C.A. Randall, T.R. Shrout, S.E. Park, P. Rehrig, Jpn. J. Appl. Phys. 41, 2099 (2002)CrossRefADS
3.
Zurück zum Zitat Y. Shimjo, R. Wang, T. Sekiya, T. Nakamura, L.E. Cross, Ferroelectrics, 284, 121 (2003)CrossRef Y. Shimjo, R. Wang, T. Sekiya, T. Nakamura, L.E. Cross, Ferroelectrics, 284, 121 (2003)CrossRef
4.
Zurück zum Zitat D.J. Fatemi, V.G. Harris, V.M. Browning, J.P. Kirkland, J. Appl. Phys. 83, 6867 (1998)CrossRefADS D.J. Fatemi, V.G. Harris, V.M. Browning, J.P. Kirkland, J. Appl. Phys. 83, 6867 (1998)CrossRefADS
5.
Zurück zum Zitat J. Xue, D. Wan, S-E. Lee, J. Wang, J. Am. Ceram. Soc. 82, 1687 (1999)CrossRef J. Xue, D. Wan, S-E. Lee, J. Wang, J. Am. Ceram. Soc. 82, 1687 (1999)CrossRef
7.
Metadaten
Titel
Preparation and characterization of high T c (1−x) BiScO3−xPbTiO3 ceramics from high energy ball milling process
verfasst von
Lin Zhang
Zhuo Xu
Zhenrong Li
Song Xia
Xi Yao
Publikationsdatum
01.12.2008
Verlag
Springer US
Erschienen in
Journal of Electroceramics / Ausgabe 1-4/2008
Print ISSN: 1385-3449
Elektronische ISSN: 1573-8663
DOI
https://doi.org/10.1007/s10832-007-9282-4

Weitere Artikel der Ausgabe 1-4/2008

Journal of Electroceramics 1-4/2008 Zur Ausgabe