Ferromagnetism in Cu-doped ZnO nanoparticles at room temperature

verfasst von: H. L. Liu, J. H. Yang, Y. J. Zhang, Y. X. Wang, M. B. Wei, D. D. Wang, L. Y. Zhao, J. H. Lang, M. Gao

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 7/2009

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Cu-doped ZnO nanoparticles were successfully synthesized and structurally characterized by using X-ray diffraction (XRD) and transmission electron microscope (TEM). XRD shows that Zn_1−xCu_xO (x ≤ 0.04) samples are single phase with the ZnO-like wurtzite structure, while the secondary phase Cu is observed in Zn_0.95Cu_0.05O sample. Magnetic measurements indicated that Zn_1−xCu_xO (x = 0.02, 0.03, 0.04) are ferromagnetic at room temperature and the magnetic moment per Cu atom decreased with increasing Cu concentration. XRD, TEM and X-ray photoelectron spectroscopy (XPS) analysis revealed that no ferromagnetic-related secondary phase was detected. The origin of the ferromagnetism in Zn_1−xCu_xO (x ≤ 0.04) was mainly due to Cu ions substituted into the ZnO lattice.

Vorheriger Artikel The hydroxyl concentration and the dielectric properties of barium titanate nano-powder synthesized by water-based ambient condition sol process

Nächster Artikel Dielectric and magnetoelectric properties of (Ni,Cu)Fe2O4 + [(Ba,Pb)(Ti,Zr)]O3 composites

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 340 Zeitschriften

aus folgenden Fachgebieten:

Bauwesen + Immobilien
Business IT + Informatik
Finance + Banking
Management + Führung
Marketing + Vertrieb
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

S.A. Wolf, D.D. Awschalom, R.A. Buhrman, J.M. Daughton, S. vonMolnar, M.L. Roukes, A.Y. Chtchelkanova, D.M. Treger, Science 294, 1488 (2001)CrossRefPubMedADS

A.P. Gary, Science 282, 1660 (1998)CrossRef

T. Dietl, H. Ohno, F. Matsukura, J. Cibert, D. Ferrand, Science 287, 1019 (2000)CrossRefPubMedADS

R. Janisch, P. Gopal, N.A. Spaldin, J. Phys. Condens. Matter. 17, R657 (2005)CrossRefADS

T.S. Herng, S.P. Lau, S.F. Yu, H.Y. Yang, L. Wang, M. Tanemura et al., Phys. Lett. 90, 032509 (2007)

H.S. Hsu, J.C.A. Huang, Y.H. Huang, Y.F. Liao, M.Z. Lin, C.H. Lee et al., Appl. Phys. Lett. 88, 242507 (2006). doi:10.1063/1.2212277 CrossRefADS

X.C. Liu, E.W. Shi, Z.Z. Chen, H.W. Zhang, B. Xiao, L.X. Song, Appl. Phys. Lett. 88, 252503 (2006)CrossRefADS

M.H. Kane, K. Shalini, C.J. Summers, R. Varatharajan, J. Nause, C.R. Vestal, Z.J. Zhang, I.T. Ferguson, J. Appl. Phys. 97, 023906 (2005)CrossRefADS

X. Liu, F. Lin, L. Sun, W. Cheng, X. Ma, W. Shi, Appl. Phys. Lett. 88, 062508 (2006)

10.

L.Q. Liu, B. Xiang, X.Z. Zhang, Y. Zhang, D.P. Yu, Appl. Phys. Lett. 88, 063104 (2006)CrossRefADS

11.

D. Karmakar, S.K. Mandal, R.M. Kadam, P.L. Paulose, A.K. Rajarajan, T.K. Nath, A.K. Das, I. Dasguptaand G.P. Das, Phys. Rev. B 75, 144404 (2007)

12.

M. Wei, N. Braddon, D. Zhi, P.A. Midgley, S.K. Chen, M.G. Blamire, J.L. MacManus-Driscoll, Appl. Phys. Lett. 86, 72514 (2005)CrossRef

13.

L.-H. Ye, A.J. Freeman, B. Delley, Phys. Rev. B 73, 033203 (2006)CrossRefADS

14.

L.M. Huang, A.L. Rosa, Phys. Rev. B 74, 075206 (2006). doi:10.1103/PhysRevB.74.075206 CrossRefADS

15.

C. Sudakar, J.S. Thakur, G. Lawes, R. Naik, V.M. Naik, B. Delley, Phys. Rev. B 75, 054423 (2007). doi:10.1103/PhysRevB.75.054423 CrossRefADS

16.

T.S. Herng, S.P. Lau, S.F. Yu, H.Y. Yang, X.H. Ji, J.S. Chen et al., J. Appl. Phys. 99, 086101 (2006). doi:10.1063/1.2190711 CrossRefADS

17.

M.H. Kane, M. Strassburg, A. Asghar, Q. Song, S. Gupta, J. Senawiratne et al., Proc. SPIE 5732, 389 (2005)CrossRefADS

18.

J.H. Yang, L.Y. Zhao, Y.J. Zhang, Y.X. Wang, H.L. Liu, M.B. Wei, Solid State Commun. 143, 566 (2007). doi:10.1016/j.ssc.2007.06.033 CrossRefADS

19.

K. Sato, H. Katayama-Yoshida, Jpn. J. Appl. Phys. 39, L555 (2000)CrossRefADS

20.

M.S. Park, B.I. Min, Phys .Rev. B 68, 224436 (2003). doi:10.1103/PhysRevB.68.224436 CrossRefADS

21.

C.-H. Chien, S.H. Chiou, G.Y. Gao, Y.-D. Yao, J. Magn. Magn. Mater. 282, 275 (2004)CrossRefADS

22.

J.H. Shim, T. Hwang, S. Lee, Appl. Phys. Lett. 86, 082503 (2005)CrossRefADS

23.

X. Wang, J.B. Xu, W.Y. Cheung, J. An, N. Ke, Appl. Phys. Lett. 90, 212502 (2007)CrossRefADS

Titel: Ferromagnetism in Cu-doped ZnO nanoparticles at room temperature
verfasst von: H. L. Liu
J. H. Yang
Y. J. Zhang
Y. X. Wang
M. B. Wei
D. D. Wang
L. Y. Zhao
J. H. Lang
M. Gao
Publikationsdatum: 01.07.2009
Verlag: Springer US
Erschienen in: Journal of Materials Science: Materials in Electronics / Ausgabe 7/2009
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI: https://doi.org/10.1007/s10854-008-9776-0

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Springer Professional "Wirtschaft"

Weitere Artikel der Ausgabe 7/2009

Rapid synthesis of stoichiometric lithium niobate powders with Li2SO4–Na2SO4 flux

Fabrication and characterization of CuInS2 films by chemical bath deposition in acid conditions

The structural and optical properties of ZnO nanowire arrays prepared by hydrothermal synthesis method

Ba2La2TiTa2O12: A new low loss microwave dielectric of A4B3O12-type cation-deficient perovskite

Synthesis, thermal, photoluminescent, and electroluminescent properties of a novel quaternary Eu(III) complex containing a carbazole hole-transporting functional group

The hydroxyl concentration and the dielectric properties of barium titanate nano-powder synthesized by water-based ambient condition sol process