Microstructure and microwave dielectric properties of Ba4.2Nd9.2Ti18−xSnxO54(x = 0, 0.25, 0.5, 1, 1.5, 2) ceramics
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 5/2015
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Ba4.2Nd9.2Ti18−xSnxO54(x = 0, 0.25, 0.5, 1, 1.5, 2) microwave dielectric ceramics with high Q × f value were prepared by conventional solid state route. The microstructure and microwave dielectric properties of Ba4.2Nd9.2Ti18−xSnxO54(x = 0, 0.25, 0.5, 1, 1.5, 2)(BNTS) ceramics were systematically investigated. XRD patterns showed that there was only a single BaNd2Ti5O14 phase identified in all samples and no second phase was found. SnO2 substitution increases the lattice parameters of BNT ceramic. Moreover, the bulk density of BNT ceramics increases as the x increases. Both the permittivity and τ
f
value decrease when the Sn concentration increases. The SnO2 substitution has a big influence on Q × f value. When x = 0.5, the BNTS ceramic gains the highest Q × f value. Afterwards, the Q × f value decreases sharply when x value increases. Excellent microwave dielectric properties were achieved in Ba4.2Nd9.2Ti18−xSnxO54(x = 0.5) ceramics sintered at 1340 °C for 2 h: ε
r
= 80.6, Q × f = 9177 GHz, τ
f
= 61 ppm/°C.