Evaluating the Diffusion Coefficient of Sulfur in Low-Silica CaO-SiO₂-Al₂O₃ Slag

The chemical diffusion coefficient of sulfur in the ternary slag of composition 51.5 pct CaO-9.6 pct SiO₂-38.9 pct Al₂O₃ slag was measured at 1680 K, 1700 K, and 1723 K (1403 °C, 1427 °C, and 1450 °C) using the experimental method proposed earlier by the authors. The \( P_{{{\text{S}}_{2} }} \) and \( P_{{{\text{O}}_{2} }} \) pressures were calculated from the Gibbs energy of the equilibrium reaction between CaO in the slag and solid CaS. The density of the slag was obtained from earlier experiments. Initially, the order of magnitude for the diffusion coefficient was taken from the works of Saito and Kawai but later was modified so that the concentration curve for sulfur obtained from the program was in good fit with the experimental results. The diffusion coefficient of sulfur in 51.5 pct CaO-9.6 pct SiO₂-38.9 pct Al₂O₃ slag was estimated to be in the range 3.98 to 4.14 × 10⁻⁶ cm²/s for the temperature range 1680 K to 1723 K (1403 °C to 1450 °C), which is in good agreement with the results available in literature