Influences of shape of the new interfaces and morphology of the intermetallics on mechanical properties of aluminum AA2024–pure copper joints by friction stir welding

verfasst von: R. Anbukkarasi, Satish V. Kailas

Erschienen in: The International Journal of Advanced Manufacturing Technology | Ausgabe 11-12/2020

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Friction stir welding (FSW) joints are inevitably accompanied with the change in shape of the abutting surfaces due to the tool movement. Further, the formation of brittle intermetallics (during dissimilar welding) is also unavoidable. Therefore, the current work is focused to study the role of the shape of the new interface in properties of the joints and to control the morphology of intermetallics subsequently. FSW experiments were carried out between aluminum AA2024 and pure copper for different tool offset positions (on either side of the interface), plate positions (copper in advancing or retreating side), and tool geometry (plain and threaded). The microstructure observation showed noticeable changes in the shape of the new interface with respect to the selected parameters. Tensile tests highlighted that the weld which has continuous and smooth new interface gave better properties than the welds which had an irregular discontinuous interface. Also, this kind of interfaces had formed with a continuous thin intermetallic layer, and it was a desirable morphology of the intermetallics. The weld with this thin intermetallic layer (metallurgical bonding) alone has the maximum strength, whereas the welds that also had fine steps at the interface (mechanical bonding from interlocking effect) have maximum ductility. The mechanism behind this was explained in detail with the help of material flow behavior study for the selected conditions. This concluded that to achieve better properties, the shape of the new interface and the bonding along this interface are mainly important to be considered.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Weigl M, Albert F, Schmidt M (2011) Enhancing the ductility of laser-welded copper-aluminum connections by using adapted filler materials. Phys Procedia 12(Part B):332–338 Weigl M, Albert F, Schmidt M (2011) Enhancing the ductility of laser-welded copper-aluminum connections by using adapted filler materials. Phys Procedia 12(Part B):332–338
2.
Zurück zum Zitat Safi SV, Amirabadi H, Besharati Givi MK, Safi SM (2016) The effect of preheating on mechanical properties of friction stir welded dissimilar joints of pure copper and AA7075 aluminum alloy sheets. Int J Adv Manuf Technol 84(9–12):2401–2411 Safi SV, Amirabadi H, Besharati Givi MK, Safi SM (2016) The effect of preheating on mechanical properties of friction stir welded dissimilar joints of pure copper and AA7075 aluminum alloy sheets. Int J Adv Manuf Technol 84(9–12):2401–2411
3.
Zurück zum Zitat Kahl S, Osikowicz W (2013) Composite aluminum-copper sheet material by friction stir welding and cold rolling. J Mater Eng Perform 22(8):2176–2184 Kahl S, Osikowicz W (2013) Composite aluminum-copper sheet material by friction stir welding and cold rolling. J Mater Eng Perform 22(8):2176–2184
4.
Zurück zum Zitat Beygi R, Kazeminezhad M, Mehrizi MZ, Eisaabadi BG, Loureiro A (2017) Friction stir butt welding of Al-Cu bilayer laminated composites: analysis of force, torque, and temperature. Int J Adv Manuf Technol 88(1–4):393–400 Beygi R, Kazeminezhad M, Mehrizi MZ, Eisaabadi BG, Loureiro A (2017) Friction stir butt welding of Al-Cu bilayer laminated composites: analysis of force, torque, and temperature. Int J Adv Manuf Technol 88(1–4):393–400
5.
Zurück zum Zitat Acarer M (2012) Electrical, corrosion, and mechanical properties of aluminum-copper joints produced by explosive welding. J Mater Eng Perform 21(11):2375–2379 Acarer M (2012) Electrical, corrosion, and mechanical properties of aluminum-copper joints produced by explosive welding. J Mater Eng Perform 21(11):2375–2379
6.
Zurück zum Zitat Sun T, Liang J, Guo X, Ren M, Wang L (2015) Optical measurement of forming limit and formability of Cu/Al clad metals. J Mater Eng Perform 24(4):1426–1433 Sun T, Liang J, Guo X, Ren M, Wang L (2015) Optical measurement of forming limit and formability of Cu/Al clad metals. J Mater Eng Perform 24(4):1426–1433
7.
Zurück zum Zitat Eslami P, Karimi Taheri A, Zebardast M (2013) A comparison between cold-welded and diffusion-bonded Al/Cu bimetallic rods produced by ECAE process. J Mater Eng Perform 22(10):3014–3023 Eslami P, Karimi Taheri A, Zebardast M (2013) A comparison between cold-welded and diffusion-bonded Al/Cu bimetallic rods produced by ECAE process. J Mater Eng Perform 22(10):3014–3023
8.
Zurück zum Zitat Kar A, Suwas S, Kailas SV (2019) Significance of tool offset and copper interlayer during friction stir welding of aluminum to titanium. Int J Adv Manuf Technol 100(1–4):435–443 Kar A, Suwas S, Kailas SV (2019) Significance of tool offset and copper interlayer during friction stir welding of aluminum to titanium. Int J Adv Manuf Technol 100(1–4):435–443
9.
Zurück zum Zitat Mishra RS, Ma ZY (2005) Friction stir welding and processing. Mater Sci Eng R Rep 50(1–2):1–78 Mishra RS, Ma ZY (2005) Friction stir welding and processing. Mater Sci Eng R Rep 50(1–2):1–78
10.
Zurück zum Zitat Kashaev N, Ventzke V, Çam G (2018) Prospects of laser beam welding and friction stir welding processes for aluminum airframe structural applications. J Manuf Process 36:571–600 Kashaev N, Ventzke V, Çam G (2018) Prospects of laser beam welding and friction stir welding processes for aluminum airframe structural applications. J Manuf Process 36:571–600
11.
Zurück zum Zitat Çam G (2011) Friction stir welded structural materials: beyond Al-alloys. Int Mater Rev 56(1):1–48 Çam G (2011) Friction stir welded structural materials: beyond Al-alloys. Int Mater Rev 56(1):1–48
12.
Zurück zum Zitat Çam G, İpekoğlu G (2017) Recent developments in joining of aluminium alloys. Int J Adv Manuf Technol 91(5–8):1851–1866 Çam G, İpekoğlu G (2017) Recent developments in joining of aluminium alloys. Int J Adv Manuf Technol 91(5–8):1851–1866
13.
Zurück zum Zitat Çam G, Mistikoglu S (2014) Recent developments in friction stir welding of al-alloys. J Mater Eng Perform 23(6):1936–1953 Çam G, Mistikoglu S (2014) Recent developments in friction stir welding of al-alloys. J Mater Eng Perform 23(6):1936–1953
14.
Zurück zum Zitat Ouyang JH, Kovacevic R (2002) Material flow and microstructure in the friction stir butt welds of the same and dissimilar aluminum alloys. J Mater Eng Perform 11(1):51–63 Ouyang JH, Kovacevic R (2002) Material flow and microstructure in the friction stir butt welds of the same and dissimilar aluminum alloys. J Mater Eng Perform 11(1):51–63
15.
Zurück zum Zitat Al-Roubaiy AO, Nabat SM, Batako ADL (2014) Experimental and theoretical analysis of friction stir welding of Al-Cu joints. Int J Adv Manuf Technol 71(9–12):1631–1642 Al-Roubaiy AO, Nabat SM, Batako ADL (2014) Experimental and theoretical analysis of friction stir welding of Al-Cu joints. Int J Adv Manuf Technol 71(9–12):1631–1642
16.
Zurück zum Zitat Sharma G, Dwivedi DK (2016) Study on microstructure and mechanical properties of dissimilar steel joint developed using friction stir welding. Int J Adv Manuf Technol:1–9 Sharma G, Dwivedi DK (2016) Study on microstructure and mechanical properties of dissimilar steel joint developed using friction stir welding. Int J Adv Manuf Technol:1–9
17.
Zurück zum Zitat Lee KJ, Kwon EP (2014) Microstructure of stir zone in dissimilar friction stir welds of AA6061-T6 and AZ31 alloy sheets. Trans Nonferrous Met Soc China (English Ed) 24(7):2374–2379 Lee KJ, Kwon EP (2014) Microstructure of stir zone in dissimilar friction stir welds of AA6061-T6 and AZ31 alloy sheets. Trans Nonferrous Met Soc China (English Ed) 24(7):2374–2379
18.
Zurück zum Zitat Fu B, Qin G, Li F, Meng X, Zhang J, Wu C (2015) Friction stir welding process of dissimilar metals of 6061-T6 aluminum alloy to AZ31B magnesium alloy. J Mater Process Technol 218:38–47 Fu B, Qin G, Li F, Meng X, Zhang J, Wu C (2015) Friction stir welding process of dissimilar metals of 6061-T6 aluminum alloy to AZ31B magnesium alloy. J Mater Process Technol 218:38–47
19.
Zurück zum Zitat Beygi R, Kazeminezhad M, Kokabi AH (2014) Microstructural evolution and fracture behavior of friction-stir-welded Al-Cu laminated composites. Metall Mater Trans A Phys Metall Mater Sci 45(1):361–370 Beygi R, Kazeminezhad M, Kokabi AH (2014) Microstructural evolution and fracture behavior of friction-stir-welded Al-Cu laminated composites. Metall Mater Trans A Phys Metall Mater Sci 45(1):361–370
20.
Zurück zum Zitat Yang CL, Wu CS, Lv XQ (2018) Numerical analysis of mass transfer and material mixing in friction stir welding of aluminum/magnesium alloys. J Manuf Process 32:380–394 Yang CL, Wu CS, Lv XQ (2018) Numerical analysis of mass transfer and material mixing in friction stir welding of aluminum/magnesium alloys. J Manuf Process 32:380–394
21.
Zurück zum Zitat Sato YS, Park SHC, Michiuchi M, Kokawa H (2004) Constitutional liquation during dissimilar friction stir welding of Al and Mg alloys. Scr Mater 50(9):1233–1236 Sato YS, Park SHC, Michiuchi M, Kokawa H (2004) Constitutional liquation during dissimilar friction stir welding of Al and Mg alloys. Scr Mater 50(9):1233–1236
22.
Zurück zum Zitat Li S, Chen Y (2019) Interfacial microstructures and mechanical properties of dissimilar titanium alloy and steel friction stir butt-welds. J Manuf Process 40:160–168 Li S, Chen Y (2019) Interfacial microstructures and mechanical properties of dissimilar titanium alloy and steel friction stir butt-welds. J Manuf Process 40:160–168
23.
Zurück zum Zitat Avettand-Fenoël MN, Taillard R, Ji G, Goran D (2012) Multiscale study of interfacial intermetallic compounds in a dissimilar Al 6082-T6/Cu friction-stir weld. Metall Mater Trans A Phys Metall Mater Sci 43(12):4655–4666 Avettand-Fenoël MN, Taillard R, Ji G, Goran D (2012) Multiscale study of interfacial intermetallic compounds in a dissimilar Al 6082-T6/Cu friction-stir weld. Metall Mater Trans A Phys Metall Mater Sci 43(12):4655–4666
24.
Zurück zum Zitat Galvão I, Loureiro A, Verdera D, Gesto D, Rodrigues DM (2012) Influence of tool offsetting on the structure and morphology of dissimilar aluminum to copper friction-stir welds. Metall Mater Trans A Phys Metall Mater Sci 43(13):5096–5105 Galvão I, Loureiro A, Verdera D, Gesto D, Rodrigues DM (2012) Influence of tool offsetting on the structure and morphology of dissimilar aluminum to copper friction-stir welds. Metall Mater Trans A Phys Metall Mater Sci 43(13):5096–5105
25.
Zurück zum Zitat Watanabe T, Takayama H, Yanagisawa A (2006) Joining of aluminum alloy to steel by friction stir welding. J Mater Process Technol 178(1–3):342–349 Watanabe T, Takayama H, Yanagisawa A (2006) Joining of aluminum alloy to steel by friction stir welding. J Mater Process Technol 178(1–3):342–349
26.
Zurück zum Zitat Tanaka T, Morishige T, Hirata T (2009) Comprehensive analysis of joint strength for dissimilar friction stir welds of mild steel to aluminum alloys. Scr Mater 61(7):756–759 Tanaka T, Morishige T, Hirata T (2009) Comprehensive analysis of joint strength for dissimilar friction stir welds of mild steel to aluminum alloys. Scr Mater 61(7):756–759
27.
Zurück zum Zitat Tan CW, Jiang ZG, Li LQ, Chen YB, Chen XY (2013) Microstructural evolution and mechanical properties of dissimilar Al-Cu joints produced by friction stir welding. Mater Des 51:466–473 Tan CW, Jiang ZG, Li LQ, Chen YB, Chen XY (2013) Microstructural evolution and mechanical properties of dissimilar Al-Cu joints produced by friction stir welding. Mater Des 51:466–473
28.
Zurück zum Zitat Li XW, Zhang DT, Qiu C, Zhang W (2012) Microstructure and mechanical properties of dissimilar pure copper/1350 aluminum alloy butt joints by friction stir welding. Trans. Nonferrous Met. Soc. China (English Ed.) 22(6):1298–1306 Li XW, Zhang DT, Qiu C, Zhang W (2012) Microstructure and mechanical properties of dissimilar pure copper/1350 aluminum alloy butt joints by friction stir welding. Trans. Nonferrous Met. Soc. China (English Ed.) 22(6):1298–1306
29.
Zurück zum Zitat Esmaeili A, Givi MKB, Rajani HRZ (2011) A metallurgical and mechanical study on dissimilar friction stir welding of aluminum 1050 to brass (CuZn30). Mater Sci Eng A 528(22–23):7093–7102 Esmaeili A, Givi MKB, Rajani HRZ (2011) A metallurgical and mechanical study on dissimilar friction stir welding of aluminum 1050 to brass (CuZn30). Mater Sci Eng A 528(22–23):7093–7102
30.
Zurück zum Zitat Xue P, Xiao BL, Ni DR, Ma ZY (2010) Enhanced mechanical properties of friction stir welded dissimilar Al-Cu joint by intermetallic compounds. Mater Sci Eng A 527(21–22):5723–5727 Xue P, Xiao BL, Ni DR, Ma ZY (2010) Enhanced mechanical properties of friction stir welded dissimilar Al-Cu joint by intermetallic compounds. Mater Sci Eng A 527(21–22):5723–5727
31.
Zurück zum Zitat Genevois C, Girard M, Huneau B (2011) Interfacial reaction during friction stir welding of Al and Cu. Metall Mater Trans A 42:2290–2295 Genevois C, Girard M, Huneau B (2011) Interfacial reaction during friction stir welding of Al and Cu. Metall Mater Trans A 42:2290–2295
32.
Zurück zum Zitat Martinez N, Kumar N, Mishra RS, Doherty KJ (2017) Effect of tool dimensions and parameters on the microstructure of friction stir welded aluminum 7449 alloy of various thicknesses. Mater Sci Eng A 684:470–479 Martinez N, Kumar N, Mishra RS, Doherty KJ (2017) Effect of tool dimensions and parameters on the microstructure of friction stir welded aluminum 7449 alloy of various thicknesses. Mater Sci Eng A 684:470–479
33.
Zurück zum Zitat Silva ACF, De Backer J, Bolmsjö G (2017) Temperature measurements during friction stir welding. Int J Adv Manuf Technol 88(9–12):2899–2908 Silva ACF, De Backer J, Bolmsjö G (2017) Temperature measurements during friction stir welding. Int J Adv Manuf Technol 88(9–12):2899–2908
34.
Zurück zum Zitat Guerra M, Schmidt C, McClure JC, Murr LE, Nunes AC (2002) Flow patterns during friction stir welding. Mater Charact 49(2):95–101 Guerra M, Schmidt C, McClure JC, Murr LE, Nunes AC (2002) Flow patterns during friction stir welding. Mater Charact 49(2):95–101
35.
Zurück zum Zitat Sun Z, Wu CS, Kumar S (2018) Determination of heat generation by correlating the interfacial friction stress with temperature in friction stir welding. J Manuf Process 31:801–811 Sun Z, Wu CS, Kumar S (2018) Determination of heat generation by correlating the interfacial friction stress with temperature in friction stir welding. J Manuf Process 31:801–811
36.
Zurück zum Zitat Kumar K, Kailas SV (2008) The role of friction stir welding tool on material flow and weld formation. Mater Sci Eng A 485(1–2):367–374 Kumar K, Kailas SV (2008) The role of friction stir welding tool on material flow and weld formation. Mater Sci Eng A 485(1–2):367–374
37.
Zurück zum Zitat Mehta KP, Badheka VJ (2015) Influence of tool design and process parameters on dissimilar friction stir welding of copper to AA6061-T651 joints. Int J Adv Manuf Technol 80(9–12):2073–2082 Mehta KP, Badheka VJ (2015) Influence of tool design and process parameters on dissimilar friction stir welding of copper to AA6061-T651 joints. Int J Adv Manuf Technol 80(9–12):2073–2082
38.
Zurück zum Zitat Rambabu G, Balaji Naik D, Venkata Rao CH, Srinivasa Rao K, Madhusudan Reddy G (2015) Optimization of friction stir welding parameters for improved corrosion resistance of AA2219 aluminum alloy joints. Def Technol 11:330–337 Rambabu G, Balaji Naik D, Venkata Rao CH, Srinivasa Rao K, Madhusudan Reddy G (2015) Optimization of friction stir welding parameters for improved corrosion resistance of AA2219 aluminum alloy joints. Def Technol 11:330–337
39.
Zurück zum Zitat Sun Z, Wu CS (2018) A numerical model of pin thread e ff ect on material fl ow and heat generation in shear layer during friction stir welding. J Manuf Process 36:10–21 Sun Z, Wu CS (2018) A numerical model of pin thread e ff ect on material fl ow and heat generation in shear layer during friction stir welding. J Manuf Process 36:10–21
40.
Zurück zum Zitat Zhou L, Zhang RX, Li GH, Zhou WL, Huang YX, Song XG (2018) Effect of pin profile on microstructure and mechanical properties of friction stir spot welded Al-Cu dissimilar metals. J Manuf Process 36:1–9 Zhou L, Zhang RX, Li GH, Zhou WL, Huang YX, Song XG (2018) Effect of pin profile on microstructure and mechanical properties of friction stir spot welded Al-Cu dissimilar metals. J Manuf Process 36:1–9
41.
Zurück zum Zitat Hasan MM, Ishak M, Rejab MRM (2017) Influence of machine variables and tool profile on the tensile strength of dissimilar AA7075-AA6061 friction stir welds. Int J Adv Manuf Technol 90(9–12):2605–2615 Hasan MM, Ishak M, Rejab MRM (2017) Influence of machine variables and tool profile on the tensile strength of dissimilar AA7075-AA6061 friction stir welds. Int J Adv Manuf Technol 90(9–12):2605–2615
42.
Zurück zum Zitat Khodir SA, Ahmed MMZ, Ahmed E, Mohamed SMR, Abdel-Aleem H (2016) Effect of intermetallic compound phases on the mechanical properties of the dissimilar Al/Cu friction stir welded joints. J Mater Eng Perform 25(11):4637–4648 Khodir SA, Ahmed MMZ, Ahmed E, Mohamed SMR, Abdel-Aleem H (2016) Effect of intermetallic compound phases on the mechanical properties of the dissimilar Al/Cu friction stir welded joints. J Mater Eng Perform 25(11):4637–4648
43.
Zurück zum Zitat Zhang QZ, Gong WB, Liu W (2015) Microstructure and mechanical properties of dissimilar Al-Cu joints by friction stir welding. Trans Nonferrous Met Soc China (English Ed) 25(6):1779–1786 Zhang QZ, Gong WB, Liu W (2015) Microstructure and mechanical properties of dissimilar Al-Cu joints by friction stir welding. Trans Nonferrous Met Soc China (English Ed) 25(6):1779–1786
44.
Zurück zum Zitat Li S, Chen Y, Zhou X, Kang J, Huang Y, Deng H (2019) High-strength titanium alloy/steel butt joint produced via friction stir welding. Mater Lett 234:155–158 Li S, Chen Y, Zhou X, Kang J, Huang Y, Deng H (2019) High-strength titanium alloy/steel butt joint produced via friction stir welding. Mater Lett 234:155–158
45.
Zurück zum Zitat Khan NZ, Siddiquee AN, Khan ZA, Shihab SK (2015) Investigations on tunneling and kissing bond defects in FSW joints for dissimilar aluminum alloys. J Alloys Compd 648:360–367 Khan NZ, Siddiquee AN, Khan ZA, Shihab SK (2015) Investigations on tunneling and kissing bond defects in FSW joints for dissimilar aluminum alloys. J Alloys Compd 648:360–367
46.
Zurück zum Zitat Xu W, Liu J, Zhu H, Fu L (2013) Influence of welding parameters and tool pin profile on microstructure and mechanical properties along the thickness in a friction stir welded aluminum alloy. Mater Des 47:599–606 Xu W, Liu J, Zhu H, Fu L (2013) Influence of welding parameters and tool pin profile on microstructure and mechanical properties along the thickness in a friction stir welded aluminum alloy. Mater Des 47:599–606
47.
Zurück zum Zitat Dressler U, Biallas G, Alfaro Mercado U (2009) Friction stir welding of titanium alloy TiAl6V4 to aluminium alloy AA2024-T3. Mater Sci Eng A 526(1–2):113–117 Dressler U, Biallas G, Alfaro Mercado U (2009) Friction stir welding of titanium alloy TiAl6V4 to aluminium alloy AA2024-T3. Mater Sci Eng A 526(1–2):113–117
48.
Zurück zum Zitat Bhattacharya TK, Das H, Jana SS, Pal TK (2017) Numerical and experimental investigation of thermal history, material flow and mechanical properties of friction stir welded aluminium alloy to DHP copper dissimilar joint. Int J Adv Manuf Technol 88(1–4):847–861 Bhattacharya TK, Das H, Jana SS, Pal TK (2017) Numerical and experimental investigation of thermal history, material flow and mechanical properties of friction stir welded aluminium alloy to DHP copper dissimilar joint. Int J Adv Manuf Technol 88(1–4):847–861
49.
Zurück zum Zitat Xue P, Ni DR, Wang D, Xiao BL, Ma ZY (2011) Effect of friction stir welding parameters on the microstructure and mechanical properties of the dissimilar Al-Cu joints. Mater Sci Eng A 528(13–14):4683–4689 Xue P, Ni DR, Wang D, Xiao BL, Ma ZY (2011) Effect of friction stir welding parameters on the microstructure and mechanical properties of the dissimilar Al-Cu joints. Mater Sci Eng A 528(13–14):4683–4689
50.
Zurück zum Zitat Lee WB, Jung SB (2004) The joint properties of copper by friction stir welding. Mater Lett 58(6):1041–1046 Lee WB, Jung SB (2004) The joint properties of copper by friction stir welding. Mater Lett 58(6):1041–1046
51.
Zurück zum Zitat Fehrenbacher A, Duffie NA, Ferrier NJ, Pfefferkorn FE, Zinn MR (2014) Effects of tool–workpiece interface temperature on weld quality and quality improvements through temperature control in friction stir welding. Int J Adv Manuf Technol 71(1–4):165–179 Fehrenbacher A, Duffie NA, Ferrier NJ, Pfefferkorn FE, Zinn MR (2014) Effects of tool–workpiece interface temperature on weld quality and quality improvements through temperature control in friction stir welding. Int J Adv Manuf Technol 71(1–4):165–179
Metadaten
Titel
Influences of shape of the new interfaces and morphology of the intermetallics on mechanical properties of aluminum AA2024–pure copper joints by friction stir welding
verfasst von
R. Anbukkarasi
Satish V. Kailas
Publikationsdatum
31.01.2020
Verlag
Springer London
Erschienen in
The International Journal of Advanced Manufacturing Technology / Ausgabe 11-12/2020
Print ISSN: 0268-3768
Elektronische ISSN: 1433-3015
DOI
https://doi.org/10.1007/s00170-019-04911-8

Weitere Artikel der Ausgabe 11-12/2020

The International Journal of Advanced Manufacturing Technology 11-12/2020 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.