Oxidation-induced micellization of a diblock copolymer containing stable nitroxyl radicals

Oxidation-induced micellization was attained for a diblock copolymer containing 2,2,6,6-tetramethylpyperidine-1-oxyl (TEMPO). Poly(4-vinylbenzyloxy-TEMPO)-block-polystyrene (PVTEMPO-b-PSt) showed no self-assembly in carbon tetrachloride, a nonselective solvent. Dynamic light scattering demonstrated that the copolymer self-assembled into micelles of 49.5-nm hydrodynamic diameter when chlorine gas was added to the copolymer solution. The UV and electron spin resonance (ESR) analyses verified that as TEMPO was oxidized into the one-electron oxidant, that is, oxoaminium chloride (OAC) by the chlorine, the nonamphiphilic block copolymer became amphiphilic in nature, and thus, the polymers underwent micellization. An investigation of the relation between the micellization and the oxidation degree of the TEMPO into the OAC revealed that the micellization was induced by only 16% of the OAC. It was confirmed that the POAC-b-PSt micelles were spherical in shape by transmission electron microscopy observation. The micelles served as a two-electron oxidizing agent for benzyl alcohol to quantitatively give benzaldehyde. The micellar structure was maintained after the oxidation of benzyl alcohol without any dissociation into unimers because the OAC was converted into an insoluble hydroxylamine–hydrochloride salt. On the other hand, the micelles reacted with N,N,N′,N′-tetramethyl-1,4-phenylenediamine (TMPD) to produce Wurster’s blue chloride by a one-electron transfer from TMPD to the OAC, converting themselves into PVTEMPO-b-PSt unimers.