Drying dissipative patterns of colloidal crystals of silica spheres in organic solvents

Drying dissipative structural patterns formed in the course of drying colloidal crystals of silica spheres (110 nm in diameter) in water, methyl alcohol, ethyl alcohol, 1-propyl alcohol, diethyl ether, and in the mixtures of ethyl alcohol with the other solvents above have been studied on a cover glass. The macroscopic broad rings were formed in the outside edges of the dried film for all the solvents examined. Furthermore, much distinct broad rings appeared in the inner area when the solvents were ethyl alcohol, methyl alcohol, and their mixtures. Profiles of the thickness of the dried films were sensitive to the organic solvents and explained well with changes in the surface tensions, boiling points, and viscosities of the solvents. The macroscopic and microscopic spoke-like crack patterns formed. The drying area (or the drying time) increased (or decreased) as the surface tension of the solvent decreased. However, the absolute values of these drying parameters are determined also by the boiling points of the solvents. Importance of the fundamental properties of the solvents is supported in addition to the characteristics of colloidal particles in the drying dissipative pattern formation.