Micelle formation induced by photolysis of a poly(tert-butoxystyrene)-block-polystyrene diblock copolymer

We found the novel photolysis-induced micellization of the poly(tert-butoxystyrene)-block-polystyrene diblock copolymer (PBSt-b-PSt). PBSt-b-PSt with a molecular weight of Mn(PBSt-b-PSt) = 15,000-b-97,000 showed no self-assembly in dichloromethane and existed as isolated copolymers with a hydrodynamic diameter of 16.6 nm. Dynamic light scattering demonstrated that the copolymer produced micelles with a 63.0 nm hydrodynamic diameter when the copolymer solution was irradiated with a high-pressure mercury lamp at room temperature in the presence of bis(alkylphenyl) iodonium hexafluorophosphate, a photoacid generator. The ¹H NMR analysis revealed that the micellization resulted from the photolysis of the PBSt blocks into insoluble poly(vinyl phenol) blocks based on the fact that the signal intensity of the tert-butyl protons decreased over time during the irradiation. It was found that the micellization rapidly proceeded as the degree of the photolysis reached over 50% and was completed at 90%.