Hybrid cement-assisted dewatering, solidification and stabilization of sewage sludge with high organic content

Sewage sludge with high organic content is particularly difficult to dewater before disposal in landfill. In this study, different hybrid cement binders were investigated to evaluate their ability to dewater the sewage sludge with high organic content. After 7 days of stabilization, the CASC (Mayenite/Sulfoaluminate cement) hybrid binder showed an excellent efficiency on both water content reduction and strength development; the water content and unconfined compressive strength value of solidified sludge reached 52.43 % and 109.55 kPa, respectively, at 8 % binder/sludge mass rate. The horizontal vibration leaching test (HJ 557-2009) indicated that leachability of heavy metals of the CASC-solidified sludge was far lower than that of non-solidified sludge and CAPC-solidified sludge. Furthermore, SEM and XRD analyses suggested that certain hydrates formed in the solidification process might have accelerated the depletion of interstitial water and strength development in the CASC-solidified sludge.