Spark-plasma-sintering temperature dependence of structural and piezoelectric properties of BNT–BT_0.08 nanostructured ceramics

(Bi_0.5Na_0.5)TiO₃ doped with 8 mol% BaTiO₃ powder prepared by sol–gel was compacted and sintered by spark-plasma-sintering method. The influence of spark-plasma-sintering temperature on the densification and piezoelectric properties of these ceramics was studied. Starting from BNT–BT_0.08 powder gel with a microstructure consisting of particles with average size of 50 nm, ceramics with grain size of 60–90 nm and density of about 98.9–99.6% of the theoretical density were obtained by spark-plasma-sintering at 800–900 °C. Increasing the sintering temperature by SPS from 800 to 900 °C lead to the increase of d ₃₃, k _p, ε ₃₃ ^T and, decrease of Q _m. Typical d ₃₃ and k _p values of BNT–BT_0.08 ceramics sintered by spark-plasma-sintering at 900 °C were 8 and 0.029, respectively.