Low-firing and microwave dielectric properties of a novel glass-free MoO3-based dielectric ceramic for LTCC applications
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 8/2019
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
A novel glass-free MoO3-based dielectric ceramic of Li2Ni2(MoO4)3 was prepared by the conventional solid-state route. The phase compositions, microstructures and microwave dielectric properties were investigated. The XRD data analysis shown that Li2Ni2(MoO4)3 belongs to an orthorhmbic lyonsite-type structure with Pmcn (62) space group during the sintering temperature range from 650 to 725 °C. The Li2Ni2(MoO4)3 ceramic could be well densification at 700 °C for 2 h with 96.8% relative density and exhibited excellent microwave dielectric properties: εr = 9.2, Q × f = 41,064 GHz, τf = − 68.86 ppm/°C. Moreover, the Li2Ni2(MoO4)3 ceramic shown excellent compatible with Ag electrode, which makes it a promising candidate for advanced substrate materials in low temperature co-fired ceramic applications.