Low temperature sintering and microwave dielectric properties of Li2ZnSiO4 ceramics with ZB glass
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 5/2013
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The influence of zinc borate (ZB) glass on densification, phase composition, microstructure and microwave dielectric properties of Li2ZnSiO4 ceramics has been investigated by using X-ray diffraction, scanning electron microscopy and Advantest network analyzer. Undoped Li2ZnSiO4 ceramics exhibited good microwave dielectric properties of ε
r
= 5.8, Q × f = 14,700 GHz and τ
f
= −96.6 ppm/°C. When ZB glass was added, the sintering temperature of Li2ZnSiO4 ceramics was effectively reduced to 950 °C. Addition of 25.wt% ZB glass to Li2ZnSiO4 ceramics sintered at 950 °C showed excellent dielectric properties of ε
r
= 5.5, Q × f = 10,800 GHz (f = 6.8 GHz) and τ
f
= −47.2 ppm/°C. Moreover, the material was compatible with Ag electrodes, making it a very promising candidate material for LTCC applications.