Mathematical Modeling on the Influence of Casting Parameters on Initial Solidification at the Meniscus of Slab Continuous Casting

In the current study, the two-dimensional mold model was applied to investigate the influence of different casting parameters on the initial solidification at the meniscus of the continuous casting mold. The profile of the meniscus and the slag rim, and the heat flux on the hot face of the copper plate, were compared with different locations of the mold and different casting parameters. The depth of the oscillation marks and solidified meniscus through simulation was measured with different casting parameters. With the mold oscillating downward from the peak to the valley, the maximum heat flux on the hot face of the copper plate near the meniscus increased from 4.3 to 5.5 MW/m², the thickness of the slag rim decreased from 4.7 to 4.2 mm, and the height of the curved meniscus also decreased. With the increase of casting speed from 1.2 to 1.45 m/min, the maximum speed of the upper backflow increased from 0.6 to 0.8 m/s, and the lowest location of the meniscus at approximately 310 mm from the copper plate decreased from 22 to 12 mm below the meniscus near the nozzle, where the slag entrapment easily occurred. With the increase of the casting speed, casting superheat, and oscillation frequency, and the decrease of the water flow rate in the mold and oscillation amplitude, the thickness of the slag rim decreased. With the increase of casting speed and superheat, and the decrease of the water flow rate in the mold, oscillation frequency, and oscillation amplitude, the depth of the solidified meniscus decreased. The regression equation was fitted to estimate the depth of hooks at the subsurface of slabs.