Mechanism of the giant permittivity in Sm modified SrTiO3 sintered at different atmospheres
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 13/2018
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The pure and Sm modified SrTiO3 ceramics have been fabricated by solid state reaction method at different atmospheres, including ambient, reduced and oxidized conditions. All studied ceramics are in single cubic perovskite phase with high bulk density, where Sm doped ceramics possess decreased grain size. The room temperature permittivities of Sr0.97Sm0.02TiO3 and Sr0.98Sm0.02TiO3 sintered in N2 were found to be on the order of 25120 and 13370 at 1 kHz with dielectric loss being 0.044 and 0.008. The giant permittivities were associated with the increase of Ti3+ ions, which were due to the combination of Ti4+ ions and electrons. With increasing Ti3+ ions, the concentration of Ti4+ ions, Ti3+ ions and \({\text{V}}_{{\text{O}}}^{{ \cdot \cdot }}\) reach the balance where the defect dipoles [\({\text{T}}{{\text{i}}^{4+}} \cdot {\text{e}} - {\text{V}}_{{\text{O}}}^{{ \cdot \cdot }} - {\text{T}}{{\text{i}}^{4+}} \cdot {\text{e}}\)] were created, responsible for the low dielectric loss.