Phase transition and electrical properties of LiNbO₃-modified K_0.49Na_0.51NbO₃ lead-free piezoceramics

Lead-free (1-x)K_0.49Na_0.51NbO₃-xLiNbO₃ (KNN-LN, x = 0 ~ 0.08) piezoelectric ceramics were prepared by the conventional solid-state sintering method. The effects of LiNbO₃ doping amount x on the phase transition behavior and the electrical properties of KNN-LN ceramics were investigated. By increasing LiNbO₃ doping amount x, the orthorhombic-tetragonal polymorphic phase transition (PPT) temperature (T _o–t) of KNN-LN ceramics shifted downwards, however, the Curie temperature (T _c) slightly moved upwards. The room temperature phase structure thus changed from orthorhombic to tetragonal across the compositions with 0.05 ≤ x ≤ 0.06, named as PPT region. The composition with x = 0.06 in the tetragonal side of PPT region exhibited optimized electrical properties of d ₃₃ = 246pC/N, k _p = 41.6%, ε _r = 679, tgδ = 0.028, and Q _m = 52. In addition to its very high T _c = 467 °C, this ceramic can be an excellent candidate for replacing the lead-based piezoceramics in high temperature applications.