Preannealing, Annealing Atmosphere, and Surface-Energy-Induced Selective Growth in 0.1 Pct Mn–Added 3 Pct Si-Fe Alloy Containing 95 ppm Sulfur
Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 5/2009
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The total number of {110} grains after final annealing increased with preannealing and was greater in a hydrogen atmosphere than under a high vacuum. Magnetic induction decreased with increasing total number of the {110} grains. This is attributed to the increase in {110} grain size, the decrease in a range for the selective growth of {100} or {111} grains, and thus the increase in number of {110} grains that show a deviation angle between the \( \langle 001\rangle \) crystal and the rolling directions.