Reliability of Steel Cylindrical Pressure Vessel Dividers in the Presence of Corrosion: Experiment and Simulation

verfasst von: N. Habibi, S. Mohammadi, H. Ghafary

Erschienen in: International Journal of Steel Structures | Ausgabe 2/2023

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The Monte Carlo simulation method can easily provide an accurate estimate of the probability of failure. However, for complex engineering problems with a low probability of failure, it may be inappropriate to provide an inefficient estimate of the probability of failure. In this study, tests investigations were performed on pressure vessel separator plates made of marine steel A36 ASTM, which exhibited corrosion on all plates, and occurred during multiple operations. The results of the tensile tests show that the areas of fracture of the specimens were observed as follows: near the gage, in the allowable area, on the line of the gage, and outside. The data obtained here provide a quantitative understanding and benchmark of the tensile behavior of corroded plates. Strain energy and maximum force varied in corrosion rate (\(\eta\)) between 10 and 24 fluctuated, while for \(\eta > 24\) decreased significantly. A series of simulations based on the Monte Carlo method was performed to determine the effects of corrosion rate and thickness variance on the overall behavior. The results of the two methods show that the values of the mechanical properties of the corroded specimens are scattered and follow a statistically normal distribution.

Vorheriger Artikel Analysis of Pressure Distribution of the Bolted Joints Based on the Finite Element Method

Nächster Artikel The Confinement Effect on the Buckling Performance of Cylindrical Tanks

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Abood, T. H. (2008). The influence of various parameters on pitting corrosion of 316L and 202 stainless. M.Sc. Thesis, Chemical Engineering Department, University of Technology, Ministry of Higher Education and Scientific Research.

Amaya-Gomezad, R., Riascos-Ochoac, J., Munoza, F., Bastidas-Arteagad, E., Schoefs, F., & Sanchez-Silva, M. (2019b). Modeling of pipeline corrosion degradation mechanism with a Lévy Process based on ILI (In-Line) inspections. International Journal of Pressure Vessels and Piping, 172, 261–271. https://doi.org/10.1016/j.ijpvp.2019.03.001CrossRef

Amaya-Gomezad, R., Sanchez-Silva, M., Bastidas-Arteaga, E., Schoefs, F., & Munoz, F. (2019a). Reliability assessments of corroded pipelines based on internal pressure: A review. Engineering Failure Analysis, 98, 190–214. https://doi.org/10.1016/j.engfailanal.2019.01.064CrossRef

American Association State Highway and Transportation Officials Standard. (2003). Standard test methods for tension testing of metallic materials. ASTM Standard. E 8-03, 1–23.

Belhamidi, S., Larif, M., Jamal, K., Elhannouni, F., & Elmidaoui, A. (2014). Demineralization of boiler feed wear for the thermal power stations: Study of mineral and organic fouling of reverse osmosis membranes. International Journal of Advanced Research in Computer Science and Software Engineering, 4(8), 86–91.

Bhardwaj, U., Teixeira, A. P., & Guedes, S. C. (2020). Uncertainty in the reliability of thick high strength pipelines with corrosion defects subjected to internal pressure. International Journal of Pressure Vessels and Piping, 188, 1–17. https://doi.org/10.1016/j.ijpvp.2020.104170CrossRef

Bhardwaj, U., Teixeira, A. P., Guedes, S. C., Samdani, A. M., Punurai, W., & Asavadorndeja, P. (2019). Reliability assessment of thick high strength pipelines with corrosion defects. International Journal of Pressure Vessels and Piping, 177, 1–12. https://doi.org/10.1016/j.ijpvp.2019.103982CrossRef

Bilyi, O. L., Dmytrakh, I. M., & Barna, R. A. (2009). Evaluation of the serviceability and fracture hazard for a Feeding pipeline with corrosion defects. Materials Science, 45(2), 238–247. https://doi.org/10.1007/s11003-009-9174-7CrossRef

Caleyo, F., Gonzalez, J. L., & Hallen, J. M. (2002). A study on the reliability assessment methodology for pipelines with active corrosion defects. International Journal of Pressure Vessels and Piping, 79(1), 77–86. https://doi.org/10.1016/j.ijpvp.2016.11.007CrossRef

Cerit, M. (2019). Corrosion pit-induced stress concentration in the spherical pressure vessel. Thin-Walled Structures, 136, 106–112. https://doi.org/10.1016/j.tws.2018.12.014CrossRef

Chaaba, A. (2013). Reliability assessment by analytical calculation of the plastic collapse load of thin pressure vessels with strain hardening and large deformation. Thin-Walled Structures, 62, 46–52. https://doi.org/10.1016/j.tws.2012.08.001CrossRef

Choi, Y., Ahn, J., & Chang, D. (2021). Time-dependent reliability analysis of plate-stiffened prismatic pressure vessel with corrosion. Mathematics, 9(13), 1–19. https://doi.org/10.3390/math9131544CrossRef

Diniz, J. L. C., Vieira, R. D., Castro, J. T., Benjamin, A. C., & Freire, J. L. F. (2006). Stress and strain analysis of pipelines with localized metal loss. Experimental Mechanics, 46(6), 765–775. https://doi.org/10.1007/s11340-006-9826-6CrossRef

Fenga, Q., Yana, B., Chena, P., & Shirazi, S. A. (2019). Failure analysis and simulation model of pinhole corrosion of the refined oil pipeline. Engineering Failure Analysis, 106, 1–28. https://doi.org/10.1016/j.engfailanal.2019.104177CrossRef

Filip, A. C., Vasiloni, M. A., Mihail, L. A., Oansea, G., & Dragogi, M. V. (2009). Experimental research on the machinability of Hardox steel by abrasive waterjet cutting. MATEC Web of Conferences, 94, 1–8. https://doi.org/10.1051/matecconf/20179403003CrossRef

Frankel, G. S. (1998). Pitting corrosion of metals: A review of the critical factors. Journal of the Electrochemical Society, 145(6), 5. https://doi.org/10.1149/1.1838748CrossRef

Gao, J., Yang, P., Li, X., Zhou, J., & Liu, J. (2019). Analytical prediction of failure pressure for the pipeline with long corrosion defect. Ocean Engineering, 191, 1–16. https://doi.org/10.1016/j.oceaneng.2019.106497CrossRef

Golchinvafa, A., Mousavi-Anijdan, S. H., Sabzi, M., & Sadeghi, M. (2020). The effect of natural inhibitor concentration of fumaria Officinalis and temperature on corrosion protection mechanism in API X80 pipeline steel in 1MH₂SO solution. International Journal of Pressure Vessels and Piping, 188, 1–9. https://doi.org/10.1016/j.ijpvp.2020.104241CrossRef

Gong, C., & Zhou, W. (2017). First-order reliability method-based system reliability analyses of corroding pipelines considering multiple defects and failure modes. Structure and Infrastructure Engineering, 13(11), 1461. https://doi.org/10.1080/15732479.2017.1285330CrossRef

Griggs, J., Lavinge, O., & Gamboa, E. (2018). Modeling 3D interaction limits of inclined stress corrosion cracking in pressurized gas pipelines. International Journal of Pressure Vessels and Piping, 168, 110–116. https://doi.org/10.1016/j.ijpvp.2019.03.001CrossRef

Guohua, C., & Shuho, D. (1996). Study on the reliability assessment methodology for pressure vessels containing defects. International Journal of Pressure Vessels and Piping, 69(3), 273–277. https://doi.org/10.1016/0308-0161(96)00010-5CrossRef

Gutman, E. M., Haddad, J., & Bergman, R. (2004). Stability of thin-walled high-pressure cylindrical pipes with variable wall thickness subjected to corrosion. In Thin-walled structures (1st edn, pp. 799–806). CRC Press, Taylor and Francis Group. ISBN: 9781351077309.

Gutman, E. M., Haddad, J., & Bergman, R. (2000). Reliability assessment by analytical calculation of the plastic collapse load of thin pressure vessels with strain hardening and large deformation. Thin-Walled Structures, 38(1), 43–52. https://doi.org/10.1016/S0263-8231(00)00024-0CrossRef

Jayanto, S. T., Chendra, M., & Wijayanta, A.T. (2019). Estimating corrosion rate and remaining life of a pressure vessel of H₂S absorber. In The 4th international conference on industrial, mechanical, electrical, and chemical engineering AIP conference proceedings (Vol. 2097, pp. 1–8). https://doi.org/10.1063/1.5098182.

Kapooria, R. K., Kumar, S., & Kasana, K. S. (2008). An analysis of a thermal power plant working on a Rankine cycle: A theoretical investigation. Journal of Energy in Southern Africa, 19(1), 77–83.CrossRef

Leira, B. J., Naess, A., & Brandrud Naess, O. E. (2013). Reliability analysis of corroding pipelines by enhanced Monte Carlo simulation. In Research, and applications in structural engineering, mechanics and computation (1st edn, pp. 737–738). CRC Press. ISBN: 9780429227769.

Li, X., & Duan, C. (2017). Design of pressure vessel cylinder based on reliability analysis, Advances in Engineering Research, 123, 623–626. In 2nd International conference on materials science, machinery and energy engineering (MSMEE 2017).

Liang, Z., Xiao, Y., & Zhang, J. (2018). Stress-strain analysis of a pipeline with inner and outer corrosion defects. Journal of Pressure Vessel and Technology, 140(6), 1–6. https://doi.org/10.1115/1.4041434CrossRef

Liu, F., Yang, Y., & Xi, F. (2020). Tensile fracture behavior of corroded pipeline: Part II: Numerical simulation based on Monte Carlo method. Advances in Materials Science and Engineering, 1–16. Article ID 5708969. https://doi.org/10.1155/2020/5708969.

Lou, X., Pathania, R., & Andersen, P. L. (2017). Effects of chloride transients on stress corrosion crack in pressure vessel low alloy steels in high-temperature water. Corrosion Science, 126, 305–316. https://doi.org/10.1016/j.corsci.2017.07.013CrossRef

Manikandan, R., & Nagarajan, K. J. (2017). Probabilistic stress analysis of cylindrical pressure vessel under internal pressure using Mont Carlo simulation method. International Journal of Current Engineering and Scientific Research, 49(4), 71–76.

McCafferty, E. (2010). Introduction to corrosion science. Springer.CrossRef

Melo, C., Dann, M., Hugo, R. J., & Janeta, A. (2020). Extreme value modeling of localized internal corrosion in unpiggable pipelines. International Journal of Pressure Vessels and Piping, 182, 1–8, 104055. https://doi.org/10.1016/j.ijpvp.2020.104055.

Metropolis, N., Rosenbluth, A. W., Rosenbluth, M. N., & Teller, A. H. (1953). Equation of state calculation by fast Computing machines. The Journal of Chemical Physics, 21, 1087–1092. https://doi.org/10.1063/1.1699114CrossRefMATH

Metropolis, N., & Ulam, S. (1949). The Monte Carlo method. Journal of the American Statistical Association, 44, 335–341. https://doi.org/10.1080/01621459.1949.10483310MathSciNetCrossRefMATH

Nie, B., Xu, S., & Wang, Y. (2020). Time-dependent reliability analysis of corroded steel beam. KSCE Journal of Civil Engineering, 24(1), 255–265. https://doi.org/10.1007/s12205-020-1478-zCrossRef

Que, Z., Seifert, H. P., Spatig, J. P., Holzer, A., Zhang, G. S., & Rao, S. R. (2019). Environmental degradation of fracture resistance in high-temperature water environments of low-alloy reactor pressure vessel steels with high sulfur or phosphorus contents. Corrosion Science, 154, 191–207. https://doi.org/10.1016/j.corsci.2019.04.011CrossRef

Rubinstein, R. Y., & Kroese, D. P. (2017). Simulation and the Monte Carlo Method (3rd ed.). Wiley.MATH

Saad-Eldeen, S., & Guedes, S. C. (2009). Effect of pitting corrosion on the collapse strength of rectangular plates under axial compression. In Analysis and design of marine structures (1st edn, pp. 231–236). CRC Press, Taylor and Francis Group. ISBN: 9780429206795.

Sakai, S., & Kaida, T. (2017). Efficient fitting procedure for corrosion rate distribution in view of reliability analysis. In ASME pressure vessels and piping conference, operations, applications, and components (Vol. 7, pp. 1–6), July 16–20, Waikoloa, Hawaii, USA. https://doi.org/10.1115/PVP2017-65030.

Schleicher, R., Raffray, R. A., & Wong, C. P. (2001). An assessment of the Brayton cycle for high-performance power plants. In Fusion technology 39(2P2): Proceedings of the fourteenth tropical meeting on the technology of fusion energy (pp. 823–827). https://doi.org/10.13182/FST01-A11963341.

Shintaku, Y., Iwamatsu, F., Suga, K., Wada, Y., & Kikuchi, M. (2015). Simulation of stress corrosion cracking in in-core monitor housing of nuclear power plant. Journal of Pressure Vessel and Technology, 137(4), 1–13. https://doi.org/10.1115/1.4028735CrossRef

Tantichattanont, P., Adluri, S. M. R., & Seshadri, R. (2007). Reliability of pipelines with corrosion defects. International Journal of Pressure Vessels and Piping, 84(12), 749–761. https://doi.org/10.1016/j.ijpvp.2006.12.004CrossRef

Teixeira, A. P., Guedes, S. C., Netto, T. A., & Stefen, S. F. N. (2008). Reliability of pipelines with corrosion defects. International Journal of Pressure Vessels and Piping, 85(4), 228–237. https://doi.org/10.1016/j.ijpvp.2007.09.002CrossRef

Vanaei, H. R., Eslami, A., & Egbewande, A. (2017). A review on pipeline corrosion, in-line inspection (ILI), and corrosion growth rate models. International Journal of Pressure Vessels and Piping, 149, 43–54. https://doi.org/10.1016/j.ijpvp.2016.11.007CrossRef

Wang, H., Yu, Y., Yu, J., Duan, J., Zhang, Y., Li, Z., & Wang, C. (2018a). Effect of 3D random pitting defects on the collapse pressure of the pipe, Part I: Experiment. Thin-Walled Structures, 129, 512–526. https://doi.org/10.1016/j.tws.2018.04.015CrossRef

Wang, H., Yu, Y., Yu, J., Jin, C., Zhao, Y., Fan, Z., & Zhang, Y. (2018b). Effect of 3D random pitting defects on the collapse pressure of the pipe, Part II: Numerical analysis. Thin-Walled Structures, 129, 527–541. https://doi.org/10.1016/j.tws.2018.04.014CrossRef

Wang, Y., Dann, M. R., & Zhang, P. (2020). Reliability analysis of corroded pipelines considering 3D Defect growth. Thin-Walled Structures, 157(1–8), 107028. https://doi.org/10.1016/j.tws.2020.107028CrossRef

Wang, Y., Wharton, J. A., & Shenoi, R. A. (2014). Ultimate strength analysis of aged steel-plated structures exposed to marine corrosion damage: A review. Corrosion Science, 86, 42–60. https://doi.org/10.1016/j.corsci.2014.04.043CrossRef

Xu, L. Y., & Cheng, Y. F. (2012). Reliability and failure pressure prediction of various grades of pipeline steel in the of corrosion defects and pre-strain. International Journal of Pressure Vessels and Piping, 89, 75–84. https://doi.org/10.1016/j.ijpvp.2011.09.008CrossRef

Yang, Y., Liu, F., & Xi, F. (2020). Tensile fracture behavior of corroded pipeline: Part I: Experimental characterization. Advances in Materials Science and Engineering, 4058452, 1–14. https://doi.org/10.1155/2020/4058452CrossRef

Zhang, S., & Zhou, W. (2014). An efficient methodology for the reliability analysis of corroding pipelines. ASME, Journal of Pressure Vessel Technology, 136(4), 041701. https://doi.org/10.1115/1.4026797CrossRef

Zhou, J. (2005). Reliability assessment method for pressure piping containing circumferential defects based on fuzzy probability. International Journal of Pressure Vessels and Piping, 82(9), 669–678. https://doi.org/10.1016/j.ijpvp.2005.04.003CrossRef

Zhou, W. (2010). System reliability of corroding pipelines. International Journal of Pressure Vessels and Piping, 87(10), 587–595. https://doi.org/10.1016/j.ijpvp.2010.07.011CrossRef

Titel: Reliability of Steel Cylindrical Pressure Vessel Dividers in the Presence of Corrosion: Experiment and Simulation
verfasst von: N. Habibi
S. Mohammadi
H. Ghafary
Publikationsdatum: 30.01.2023
Verlag: Korean Society of Steel Construction
Erschienen in: International Journal of Steel Structures / Ausgabe 2/2023
Print ISSN: 1598-2351
Elektronische ISSN: 2093-6311
DOI: https://doi.org/10.1007/s13296-023-00715-5

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 2/2023

Web Stress Development Mechanism Critical for the Fatigue Limit State in Horizontally Curved Steel Bridges

Push-Out Tests on Interlocked Angles Connectors in Steel-Concrete-Steel Composite Structure

Examination of Gusset Plate Modeling via Nonlinear Dynamic Analysis

Experimental and Numerical Study on the Collapsing Behavior of Structural Systems with Steel Members Arranged in Parallel Under Tension

Experimental Study on Structural Performance of New Steel–Concrete Composite Beam for Both Long-Span and Low-Height Parking Structures

Study of Fire Resistance Performance of Stiffened Welded Hollow Spherical Joint Under Axial Tension

Premium Partner

Marktübersichten