09.03.2023 | Ceramics

Repair of surface cracks in 3D-printed porous ceramic skeletons after sintering

verfasst von: Huan Wang, Ziyuan Li, Zhen Shang, Limei Tian

Erschienen in: Journal of Materials Science | Ausgabe 12/2023

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Porous ceramics have a wide range of applications in areas such as energy storage, heat transfer and sewage treatment. One of the common preparation methods of porous ceramics is photocuring 3D printing technology. However, many cracks inevitably appear on the surface of the porous ceramic skeleton after sintering. These cracks impair the mechanical properties and thermal conductivity of the porous ceramic skeleton, accelerate its corrosion rate, and limit its engineering applications. Therefore, methods to repair cracks on the surface of porous ceramics are urgently required. In this work, the green body of the porous ceramic skeleton was prepared by a liquid crystal display 3D printer. Two kinds of porous ceramic skeleton were prepared, either by high-temperature sintering in an inert atmosphere or by liquid silicon infiltration. The cracks on the surface of the two kinds of porous ceramic skeleton were repaired by impregnation followed by secondary sintering. After secondary sintering, a porous ceramic skeleton with superior performance was obtained. Experimental results showed that the porosity of porous ceramic skeleton after high-temperature sintering in an inert atmosphere and liquid silicon infiltration was 76.39% and 72.30%, respectively. After the crack repair, the porosity of porous ceramic skeleton decreased by 4.64% and 4.33%, respectively. However, the compressive stress of the porous ceramic skeleton increased by 12.78 times and 4.56 times, and the heat transfer efficiency increased by 15.38% and 12.12%, respectively. Therefore, this study provides a method for crack repair on the surface of ceramic skeletons, which is of great significance for the improvement of mechanical properties and thermal conductivity of the porous ceramic skeleton.

Vorheriger Artikel Metal–organic framework–carbon allotrope composites as emerging effective and superdurable nanofillers: progress in design and application

Nächster Artikel Preparation and microstructure analysis of fly ash continuous fiber

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Ohji T, Fukushima M (2012) Macro-porous ceramics: processing and properties. Int Mater Rev 57(2):115–131CrossRef

Chen Y, Wang NN, Ola O, Xia YD, Zhu YQ (2021) Porous ceramics: light in weight but heavy in energy and environment technologies. Mat Sci Eng R 143:100589CrossRef

Chen ZW, Li ZY, Li JJ, Liu CB, Lao CS, Fu YL, Liu CY, Li Y, Wang P, He Y (2019) 3D printing of ceramics: a review. J Eur Ceram Soc 39(4):661–687CrossRef

Lurie SA, Solyaev YO, Rabinskiy LN, Polyakov PO, Sevostianov I (2018) Mechanical behavior of porous Si₃N₄ ceramics manufactured with 3D printing technology. J Mater Sci 53(7):4796–4805. https://doi.org/10.1007/s10853-017-1881-0CrossRef

Eckel ZC, Zhou CY, Martin JH, Jacobsen AJ, Carter WB, Schaedler TA (2016) 3D printing additive manufacturing of polymer-derived ceramics. Science 351(6268):58–62CrossRef

Lan WW, Huang XB, Huang D, Wei XC, Chen WY (2022) Progress in 3D printing for bone tissue engineering: a review. J Mater Sci 57(27):12685–12709. https://doi.org/10.1016/j.bioactmat.2020.01.004CrossRef

Fu YL, Chen ZW, Xu G, Wei Y, Lao CS (2019) Preparation and stereolithography 3D printing of ultralight and ultrastrong ZrOC porous ceramics. J Alloy Compd 789:867–873CrossRef

Cheng P, Peng Y, Wang K, Duigou AL, Yao S, Chen C (2023) Quasi-static penetration property of 3D printed woven-like ramie fiber reinforced biocomposites. Compos Struct 303:116313CrossRef

Felzmann R, Gruber S, Mitteramskogler G, Tesavibul P, Boccaccini AR, Liska R, Stampfl J (2012) Lithography-based additive manufacturing of cellular ceramic structures. Adv Eng Mater 14(12):1052–1058CrossRef

10.

Zhang H, Yang Y, Hu KH, Liu B, Liu M, Huang ZR (2020) Stereolithography-based additive manufacturing of lightweight and high-strength C_f/SiC ceramics. Addit Manuf 34:101199

11.

Zanchetta E, Cattaldo M, Franchin G, Schwentenwein M, Homa J, Brusatin G, Colombo P (2016) Stereolithography of SiOC ceramic microcomponents. Adv Mater 28(2):370–376CrossRef

12.

Liang X, Li YW, He Z, Yan W, Tan FG, Wang QH, Zhu TB, Sang SB (2021) The effect of cellular structure on the strength and combustion properties of SiC porous ceramics. Ceram Int 48(2):2538–2545CrossRef

13.

Song X, Chen Y, Lee TW, Wu SH, Cheng LX (2015) Ceramic fabrication using mask-image-projection-based stereolithography integrated with tape-casting. J Manuf Process 20(3):456–464CrossRef

14.

Maeng WY, Lee JB, Koh YH, Kim HE (2019) Innovative in situ photocuring-assisted 3D plotting technique for complex-shaped ceramic architectures with high shape retention. Ceram Int 45(7):8440–8447CrossRef

15.

Johansson E, Lidstrom O, Johansson J, Lyckfeldt O, Adolfsson E (2017) Influence of resin composition on the defect formation in alumina manufactured by stereolithography. Materials 10(2):138CrossRef

16.

Rasaki SA, Xiong DY, Xiong SF, Su F, Idrees M, Chen ZW (2021) Photopolymerization-based additive manufacturing of ceramics: a systematic review. J Adv Ceram 10(3):442–471CrossRef

17.

Stumpf M, Travitzky N, Greil P, Fey T (2018) Sol-gel infiltration of complex cellular indirect 3D printed alumina. J Eur Ceram Soc 38(10):3603–3609CrossRef

18.

Wang SR, Geng HR, Hui LH, Wang YZ (2017) Reticulated porous multiphase ceramics with improved compressive strength and fracture toughness. J Mater Eng Perform 16(1):113–118CrossRef

19.

Zhou M, Zeng LK, Cheng XS, Wang H, Liu PA (2011) Preparation of large effective specific surface area reticulate porous ceramics by polymeric foam replication process using recoating technique. Rare Met 38:418–421CrossRef

20.

Baux A, Goillot A, Jacques S, Heisel C, Rochais D, Charpentier L, David P, Piquero T, Chartier T, Chollon G (2020) Synthesis and properties of macroporous SiC ceramics synthesized by 3D printing and chemical vapor infiltration/deposition. J Eur Ceram Soc 40(8):2834–2854CrossRef

21.

Maleksaeedi S, Eng H, Wiria FE, Ha TMH, He Z (2014) Property enhancement of 3D-printed alumina ceramics using vacuum infiltration. J Mater Process Tech 214(7):1301–1306CrossRef

22.

Mamatha S, Biswas P, Das D, Johnson R (2019) Fabrication of complex shaped ceramic articles from 3D printed polylactic acid templates by replication process. Ceram Int 45(15):19577–19580CrossRef

23.

DeVries M, Subhash G, Mcghee A, Ifju P, Jones T, Zheng J, Halls V (2018) Quasi-static and dynamic response of 3D-printed alumina. J Eur Ceram Soc 38(9):3305–3316CrossRef

24.

Song SY, Park MS, Lee JW, Yun JS (2018) Improvement of dispersion stability and 3D-printing characteristics of ceramics in photopolymers by controlling the coating thickness of silane coupling agents. Mater Chem Phys 216:446–453CrossRef

25.

Fleisher A, Zolotaryov D, Kovalevsky A, Muller-Kamskii G, Eshed E, Kazakin M, Popov V (2019) Reaction bonding of silicon carbides by Binder Jet 3D-Printing, phenolic resin binder impregnation and capillary liquid silicon infiltration. Ceram Int 45(14):18023–18029CrossRef

26.

Wang H, Li ZY, Shang Z, Tian LM (2022) Preparation of porous SiC ceramics skeleton with low-cost and controllable gradient based on liquid crystal display 3D printing. J Eur Ceram Soc 42(13):5432–5437CrossRef

27.

Liu XL, Wang HL, Xu Q, Luo QY, Song YA, Tian Y, Chen M, Xuan YM, Jin Y, Jia YX, Li YL, Ding YL (2021) High thermal conductivity and high energy density compatible latent heat thermal energy storage enabled by porous AlN ceramics composites. Int J Heat Mass Trans 175:121405CrossRef

28.

Liden E, Karlsson S, Tokarz B (2001) Silica sols as refractory fibre binders. J Eur Ceram Soc 21:795–808CrossRef

29.

Gordeeva SS, Kozlovskii AG, Askinazi YV, Suvorov SA (2010) Unmolded refractories with a silica sol binder. Refract Ind Ceram 51(4):272–273CrossRef

30.

Kong DY, Yang H, Wei S, Li DY, Wang JB (2007) Gel-casting without de-airing process using silica sol as a binder. Ceram Int 33:133–139CrossRef

31.

Li H, Liu YS, Colombo P, Li WB, Liu YS, Hu KH, Lu ZG (2022) Enhanced 3D printed alumina ceramic cores via impregnation. J Am Ceram Soc 105(1):181–192CrossRef

32.

Tang J, Liu M, Wei YQ, Yang Y, Huang ZR (2021) An efficient and low-cost liquid silicon infiltration method to prepare SiC-coated carbon short fiber for fiber protection of C-f/SiC ceramic matrix composites. Ceram Int 47(9):13235–13241CrossRef

33.

Zhang J, Jiang JM, Song Q, Pan T, Wu ZQ, Jia XZ, Wen Y (2021) Ultra-high temperature ablation property of Ta_0.5Hf_0.5C ternary ceramic under plasma flame. Ceram Int 47(19):28050–28054CrossRef

34.

Liang X, Li YM, Sang SB, Wang QH, He Z, Li BW (2020) The hydration resistance, evolution mechanism of sol-coated aluminum and its effect on mechanical properties of SiC reticulated porous ceramics. Ceram Int 46(8):11246–11254CrossRef

35.

Zhang C, Luo ZQ, Liu CB, Zhu JY, Cao JW, Yuan JK, Wang P, Liu CY, Lao CS, Chen ZW (2021) Dimensional retention of photocured ceramic units during 3D printing and sintering processes. Ceram Int 47(8):11097–11108CrossRef

36.

Xiong JQ, Peng YT, Xie DY, Mao XS (2012) The characteristics of silica-sol combining refractories. Adv Mater Res 396–398:288–291

Titel: Repair of surface cracks in 3D-printed porous ceramic skeletons after sintering
verfasst von: Huan Wang
Ziyuan Li
Zhen Shang
Limei Tian
Publikationsdatum: 09.03.2023
Verlag: Springer US
Erschienen in: Journal of Materials Science / Ausgabe 12/2023
Print ISSN: 0022-2461
Elektronische ISSN: 1573-4803
DOI: https://doi.org/10.1007/s10853-023-08317-6

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 12/2023

Exploring supervised machine learning for multi-phase identification and quantification from powder X-ray diffraction spectra

Two-dimensional Nb2CTx nanosheets decorated LiFePO4/C as cathode material for lithium-ion batteries

Microfluidics-assisted, time-effective and continuous synthesis of bimetallic ZIF-8/67 under different synthesis conditions

Identification of a pseudo-ternary intermetallic compound in the stirred zone of friction-stir-welded 5083 aluminum alloy with 316L steel

Palladium exsolution and dissolution with lanthanum ferrite perovskite oxides

Uniformly embedded PtCu alloy nanoparticles on mesoporous carbon nanospheres: a high-efficiency nanozyme for glucose detection

Premium Partner

Marktübersichten