Structural, magnetic and magnetoelectric properties of the magnetoelectric composite material
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 9/2014
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
(x) CoFe2O4 + (1 − x) Ba0.9Sr0.1TiO3 magnetoelectric (ME) composites with x = 0.1, 0.2, 0.3, 0.4 and 0.5 were prepared by a conventional standard double sintering ceramic method. The magnetic and ME properties of composites consisting of cobalt ferrite (CoFe2O4) and barium strontium titanate (Ba0.9Sr0.1TiO3) were investigated. The X-ray diffraction analysis was carried out to confirm the phases formed during sintering and also to calculate the lattice parameters. The hysteresis measurements were done to determine saturation magnetization (Ms), remanence magnetization (Mr) and coercivity (Hc) of the samples. The ME voltage coefficient (dE/dH)H was studied as a function of intensity of the magnetic field. The measured ME response demonstrated strong dependence on the volume fraction of CoFe2O4 and the applied magnetic field. A large ME voltage coefficient of about 1,380 µV/cm/Oe was observed for 10 % CoFe2O4 + 90 % Ba0.9Sr0.1TiO3 composite.