Structure and dielectric properties of potassium niobate nano glass–ceramics
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 7/2011
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Glasses in the composition of 25K2O-25Nb2O5-50SiO2 (mol %) have been prepared by melt quenching technique and isothermally heat-treated at 800 °C for different duration (0–200 h). The formed nanocrystalline KNbO3 phase, crystallite size and morphology are examined by X-ray diffraction, Fourier transform infrared reflection spectroscopy, field emission scanning and transmission electron microscopes. The frequency and temperature dependent dielectric constant and loss tangent are measured in the frequency and temperature ranges 0.1–1000 kHz and 200–500 °C respectively. The dielectric constant and loss tangent are found to decrease with increasing frequency and increase with increasing temperature. The dielectric constant and loss tangent versus temperature curve at different frequency revealed the phase transition of KNbO3 from paraelectric cubic to ferroelectric tetragonal around 425 and 397 °C (Curie temperature) for nano glass–ceramics obtained after 1 and 200 h heat-treatment respectively.