Studies of structural, impedance spectroscopy and magnetoelectric properties of (SmLi)_1/2(Fe_2/3Mo_1/3)O₃ electroceramics

In the present communication, studies of some physical properties (i.e., crystal data, permittivity, impedance, electrical cobnduction and magnetic) of a multiferroic material with a chemical composition (SmLi)_1/2(Fe_2/3Mo_1/3)O₃ have been reported. Thermogravimetric analysis of the compound, prepared by cost effective ceramic technology processing, was executed to check the mass loss as well as the required decomposition temperature of the ingredients. An analysis of X-ray spectra or pattern suggests that the crystallization phase or cystal system of the compound at room temperature is orthorhombic. The broad studies of dielectric properties {relative dielectric constant (ε_r), and tangent loss (tan δ)} display their independence of temperature and frequency in the rage of (30–375 °C) and (1 kHz–1 MHz) respectively. The impedance spectroscopic technique has provided a considerable significant information regarding the grain, grain boundary contribution within the sample and relaxation mechanism of the compound. The occurrence of negative temperature coefficient behaviour (NTCR) is depicted by the further analysis of impedance parameters. The frequency–temperature dependence of conductivity follows the Johnson’s power Universal law. The Arrhenius plot (i.e., variation of electrical conductivity with temperature) is used to calculate the activation energy. Analysis of magnetization (M–H) loop shows weak ferromagnetism of the compound. The material possesses significantly high magnitude of magnetoelectric coefficient of 3.0 mV Cm^− 1 Oe^− 1.