Synthesis and luminescent properties of Sr4Al14O25:Eu2+ blue–green emitting phosphor for white light-emitting diodes (LEDs)
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 4/2008
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
An efficient blue–green emitting phosphor, Sr4Al14O25:Eu2+, was prepared by solid-state reaction. X-ray powder diffraction (XRD) analysis confirmed the formation of Sr4Al14O25:Eu2+. Field-emission scanning electron-microscopy (FE-SEM) observation indicated that the microstructure of the phosphor consisted of irregular fine grains with an average size of about 8–10 μm. Photoluminescence measurements showed a broad absorption band between 300 and 450 nm which was efficiently excited by near-ultraviolet (NUV) LEDs (350–410 nm) and a strong emission band peaking at 491 nm. A bright blue–green LED with chromatic coordination (0.176, 0.412) was fabricated by incorporating the phosphor with an InGaN-based NUV chip, which indicates that Sr4Al14O25:Eu2+ is a good candidate phosphor for application in white LEDs.