Synthesis and magnetic properties of Ni–Fe/Cu/Co/Cu multilayer nanowire arrays
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 4/2015
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Ni–Fe/Cu/Co/Cu multilayer nanowire arrays were successfully electrodeposited into pores of an AAO template using a three-bath method. TEM and SEM were used to characterize structure and morphology of multilayered nanowire arrays. The results indicate that layer thickness is very uniform and multilayered structure is clear and regular. Multilayered nanowire arrays are highly ordered. Average diameter of multilayered nanowires is about 120 nm, which is the same as pore diameter of AAO templates. Vibrating sample magnetometer and physical property measurement system reveal that magnetic coercivity in an applied magnetic field perpendicular to surface of AAO templates is larger than the coercive field parallel to the surface of AAO templates. CPP GMR of Ni–Fe/Cu/Co/Cu nanowire arrays is affected by change of copper layer thickness.