Synthesis and study of structural, dielectric, magnetic and magnetoelectric properties of K_0.5Na_0.5NbO₃–CoMn_0.2Fe_1.8O₄ composites

Magnetoelectric (ME) composites consisting of K_0.5Na_0.5NbO₃ (KNN) as ferroelectric phase and CoMn_0.2Fe_1.8O₄ (CMFO) as ferrite phase with general formula (x) CoMn_0.2Fe_1.8O₄–(1 − x) K_0.5Na_0.5NbO₃ (x = 10, 20, 30, 40 and 50 wt%) were synthesized using solid state reaction method. X-ray diffraction analysis asserts the existence of component phases including spinel phase of CMFO and orthorhombic phase of KNN. Field emission scanning electron microscopy has been used for studying the morphology and calculation of average grain size. The temperature dependent dielectric properties including dielectric constant (\(\varepsilon ^{\prime}\)) and dielectric loss (tan δ) at different frequencies has been studied and both are found to increase with incorporation of CMFO. Magnetic hysteresis loops have been measured at temperatures of 300 and 5 K. Variation of magnetization versus temperature has been studied in field cooled and zero field cooled modes. Polarization versus electric field (P–E) hysteresis loops are obtained at room temperature indicating presence of ferroelectric ordering in the composites at room temperature. The remnant polarization (2P_r) and coercive field (2E_c) are found to decrease linearly with incorporation of CMFO. ME voltage coefficient (α_ME) has been measured. The maximum value of α_ME is found to be 5.941 mV/cm-Oe for 10% CMFO–90% KNN bulk composite.