Temperature-dependent ferroelectric hysteresis properties of modified lead zirconate titanate ceramics

Temperature-dependent ferroelectric hysteresis properties of modified lead zirconate titanate ceramics have been investigated in a wide temperature range from 300 to 433 K. It is observed that remnant polarization, saturation polarization, and coercive field are increasing with an increase of the temperature in a low-field region and decreasing in a high-field region. Such behavior is explained by the competition between switching and backswitching mechanisms. A three-stage dependence of the logarithm of the hysteresis loop area on the logarithm of the electric field is identified. The temperature dependence of backswitching properties has been studied. The obtained results indicate that the temperature dependence of the polarization backswitching can be well described by the Arrhenius law. The activation energy for the domain switching determined from the fitting results exhibits decreasing tendency with the increase of the electric field.