Thermal annealing of LaF₃:Eu³⁺ nanocrystals synthesized by a solvothermal method and their luminescence properties

In this work, we used a low temperature solvothermal method to synthesize Eu³⁺-doped LaF₃ (LaF₃:Eu³⁺) nanocrystals. The effect of thermal annealing on their phase structures and luminescence properties was studied. Transformation from LaF₃ to LaOF was observed after the annealing, and the initial transformation process was studied using a rapid thermal annealing technique. It was found that a sufficiently high annealing temperature is required for the transformation of LaF₃ to LaOF. LaOF phase started to be formed after annealing at 500 °C for as short as 5 min, and higher annealing temperatures and longer annealing time led to a larger amount of LaOF formed. With the increase of the formation of LaOF, the luminescence was greatly enhanced. Strong O²⁻ → Eu³⁺ charge transfer band was present in these samples annealed at 500 °C and higher temperatures, and greatly enhanced ⁷F₀ → ⁵D₂ transition of Eu³⁺ was also observed.